Refractory Metal NbTi-ANN vs NbTi CW+HT
Refractory Metal · NbTi temper comparison
NbTi-ANN and NbTi CW+HT are two conditions of the same refractory metal grade, NbTi: ANN (annealed) versus CW+HT (cold drawn with intermediate α-Ti precipitation heat treatments). The chemistry is identical, so every difference below comes from the condition. NbTi CW+HT is the stronger of the two: yield strength 930 MPa (135 ksi) against 350 MPa (50.8 ksi) for NbTi-ANN, about 166% more; tensile strength follows at 1,050 MPa (152 ksi) vs 620 MPa (89.9 ksi). In exchange, NbTi-ANN is the more ductile: elongation 25% versus 5% for NbTi CW+HT, and NbTi CW+HT is harder (260 HB vs 160 HB). NbTi CW+HT is stiffer (70 GPa vs 65 GPa) and NbTi-ANN runs hotter in service (400°C vs 300°C continuous). On the shop floor, NbTi-ANN welds better (fair vs poor).
NbTi-ANNChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
NbTi CW+HTChoose it when strength drives the design.
NbTi-ANN vs NbTi CW+HT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all refractory metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 24 GPa3.5 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 6.05 g/cm³0.22 lb/in³ · Melting Point (Solidus) 1,900°C3,452 °F · Liquidus Temperature 2,020°C3,668 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 350 J/kg·K0.08 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8 µm/m·K4.4 µin/in·°F · Latent Heat of Fusion 290 J/g125 BTU/lb · Min Service Temperature -271°C-456 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V · Corrosion Resistance 85 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 25 / 100 · Brazeability / Solderability 40 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 700 MJ/kg300,946 BTU/lb · Embodied Carbon (primary production) 45 kg CO₂/kg · Typical Recycled Content 10%
Strength versus weight
Yield strength against density for every refractory metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
NbTi-ANN vs NbTi CW+HT — frequently asked
Is NbTi CW+HT stronger than NbTi-ANN?
Yes. NbTi CW+HT has a typical yield strength of 930 MPa (135 ksi) against 350 MPa (50.8 ksi) for NbTi-ANN — about 166% more. Tensile strength is 1,050 MPa (152 ksi) vs 620 MPa (89.9 ksi).
Which condition does FabDigit quote by default, ANN or CW+HT?
ANN is the default NbTi condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, NbTi-ANN or NbTi CW+HT?
NbTi-ANN, by a small margin. Both rate poor for machinability — 20/100 against 15/100 for NbTi CW+HT; for welding the order is NbTi-ANN first (fair, 45/100) then NbTi CW+HT (poor, 30/100).