Precious Metal PdRu5-H01 vs PdRu5 Spring
Precious Metal · PdRu5 temper comparison
PdRu5-H01 and PdRu5 Spring are two conditions of the same precious metal grade, PdRu5: H01 (quarter hard) versus Spring (spring hard). The chemistry is identical, so every difference below comes from the condition. PdRu5 Spring is the stronger of the two: yield strength 960 MPa (139 ksi) against 450 MPa (65.3 ksi) for PdRu5-H01, about 113% more; tensile strength follows at 1,050 MPa (152 ksi) vs 600 MPa (87 ksi). In exchange, PdRu5-H01 is the more ductile: elongation 12% versus 1.5% for PdRu5 Spring, and PdRu5 Spring is harder (250 HB vs 152 HB). PdRu5-H01 runs hotter in service (450°C vs 250°C continuous). On the shop floor, PdRu5 Spring machines more easily (fair vs poor) and PdRu5-H01 welds better (good vs fair).
PdRu5-H01Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
PdRu5 SpringChoose it when strength drives the design, or when the part is machined in volume.
PdRu5-H01 vs PdRu5 Spring: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 50 GPa7.3 Msi · Bulk Modulus 195 GPa28.3 Msi · Poisson's Ratio 0.39
Physical
Density and transition temperatures.
Same in both: Density 12.05 g/cm³0.44 lb/in³ · Melting Point (Solidus) 1,575°C2,867 °F · Liquidus Temperature 1,600°C2,912 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 245 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 157 J/g67.5 BTU/lb · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.2 V · Corrosion Resistance 92 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 80 / 100 · Polishability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 95,000 MJ/kg4.08×10⁷ BTU/lb · Embodied Carbon (primary production) 3,800 kg CO₂/kg · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PdRu5-H01 vs PdRu5 Spring — frequently asked
Is PdRu5 Spring stronger than PdRu5-H01?
Yes. PdRu5 Spring has a typical yield strength of 960 MPa (139 ksi) against 450 MPa (65.3 ksi) for PdRu5-H01 — about 113% more. Tensile strength is 1,050 MPa (152 ksi) vs 600 MPa (87 ksi).
Which condition does FabDigit quote by default, H01 or Spring?
Annealed is the default PdRu5 condition in the FabDigit quote flow (neither H01 nor Spring). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, PdRu5-H01 or PdRu5 Spring?
PdRu5 Spring. Its machinability rates fair (40/100) against poor (30/100) for PdRu5-H01; for welding the order is PdRu5-H01 first (good, 60/100) then PdRu5 Spring (fair, 45/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in PdRu5-H01 and PdRu5 Spring side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.