Precious Metal Pd60Ag40-H06 vs Pd60Ag40-O
Precious Metal · Pd60Ag40 temper comparison
Pd60Ag40-H06 and Pd60Ag40-O are two conditions of the same precious metal grade, Pd60Ag40: H06 (extra hard) versus O (annealed). The chemistry is identical, so every difference below comes from the condition. Pd60Ag40-H06 is the stronger of the two: yield strength 780 MPa (113 ksi) against 180 MPa (26.1 ksi) for Pd60Ag40-O, about 4.3 times as much; tensile strength follows at 830 MPa (120 ksi) vs 415 MPa (60.2 ksi). In exchange, Pd60Ag40-O is the more ductile: elongation 30% versus 2% for Pd60Ag40-H06, and Pd60Ag40-H06 is harder (197 HB vs 80 HB). Pd60Ag40-O runs hotter in service (500°C vs 230°C continuous). On the shop floor, Pd60Ag40-H06 machines more easily (48 vs 35 out of 100) and Pd60Ag40-O welds better (very good vs good).
Pd60Ag40-H06Choose it when strength drives the design, or when the part is machined in volume.
Pd60Ag40-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Pd60Ag40-H06 vs Pd60Ag40-O: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 40 GPa5.8 Msi · Bulk Modulus 145 GPa21 Msi · Poisson's Ratio 0.37
Physical
Density and transition temperatures.
Same in both: Density 11.35 g/cm³0.41 lb/in³ · Melting Point (Solidus) 1,290°C2,354 °F · Liquidus Temperature 1,330°C2,426 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 240 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 14.5 µm/m·K8.1 µin/in·°F · Latent Heat of Fusion 136 J/g58.5 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.2 V · Corrosion Resistance 92 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 70 / 100 · Brazeability / Solderability 85 / 100 · Polishability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 44,000 MJ/kg1.89×10⁷ BTU/lb · Embodied Carbon (primary production) 2,400 kg CO₂/kg · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Pd60Ag40-H06 vs Pd60Ag40-O — frequently asked
Is Pd60Ag40-H06 stronger than Pd60Ag40-O?
Yes. Pd60Ag40-H06 has a typical yield strength of 780 MPa (113 ksi) against 180 MPa (26.1 ksi) for Pd60Ag40-O — about 4.3 times as much. Tensile strength is 830 MPa (120 ksi) vs 415 MPa (60.2 ksi).
Which condition does FabDigit quote by default, H06 or O?
O is the default Pd60Ag40 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, Pd60Ag40-H06 or Pd60Ag40-O?
Pd60Ag40-H06, by a small margin. Both rate fair for machinability — 48/100 against 35/100 for Pd60Ag40-O; for welding the order is Pd60Ag40-O first (very good, 75/100) then Pd60Ag40-H06 (good, 60/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Pd60Ag40-H06 and Pd60Ag40-O side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.