Precious Metal BAg-2a vs BAg-9
Precious Metal · grade comparison
Precious Metal BAg-2a and BAg-9 are both precious metal grades. BAg-2a is the stronger of the two: yield strength 210 MPa (30.5 ksi) against 170 MPa (24.7 ksi) for BAg-9, about 24% more; tensile strength follows at 400 MPa (58 ksi) vs 380 MPa (55.1 ksi). In exchange, BAg-9 is the more ductile: elongation 32% versus 28% for BAg-2a, and BAg-2a is harder (95 HV vs 90 HV). BAg-2a is lighter (9.4 g/cm³ vs 9.8 g/cm³ for BAg-9) and BAg-2a is stiffer (90 GPa vs 85 GPa). On the shop floor, BAg-9 welds better (30 vs 20 out of 100).
BAg-2aChoose it when strength drives the design, or when weight is the constraint.
BAg-9Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
BAg-2a vs BAg-9: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Hardness, Vickers
Reduction in Area
Fatigue Strength (Endurance Limit)
Hardness, Rockwell B
Same in both: Poisson's Ratio 0.36 · Hardness, Brinell 85 HB
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Same in both: Thermal Expansion (CTE, 20–100 °C) 19 µm/m·K10.6 µin/in·°F · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Machinability Rating (AISI 1212 = 100 %)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 2,500 L/kg300 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | BAg-2a | BAg-9 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
BAg-2a vs BAg-9 — frequently asked
Is BAg-2a stronger than BAg-9?
Yes. BAg-2a has a typical yield strength of 210 MPa (30.5 ksi) against 170 MPa (24.7 ksi) for BAg-9 — about 24% more. Tensile strength is 400 MPa (58 ksi) vs 380 MPa (55.1 ksi).
Which is cheaper, BAg-2a or BAg-9?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, BAg-2a or BAg-9?
BAg-2a, by a small margin. Both rate fair for machinability — 45/100 against 40/100 for BAg-9; for welding the order is BAg-9 first (poor, 30/100) then BAg-2a (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in BAg-2a and BAg-9 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.