Precious Metal BAg-2a and BAg-33 are both precious metal grades. BAg-33 is the stronger of the two: yield strength 240 MPa (34.8 ksi) against 210 MPa (30.5 ksi) for BAg-2a, about 14% more. In exchange, BAg-2a is the more ductile: elongation 28% versus 22% for BAg-33, and BAg-33 is harder (105 HB vs 85 HB). BAg-2a is stiffer (90 GPa vs 85 GPa) and BAg-33 runs hotter in service (250°C vs 200°C continuous).
BAg-2aChoose it when the part is bent, formed or impact-loaded.
BAg-33Choose it when strength drives the design, or when the part sees heat.
BAg-2a vs BAg-33: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Hardness, Brinell
Hardness, Vickers
Same in both: Tensile Strength (Ultimate) 400 MPa58 ksi
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 607°C1,125 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Machinability 45 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Strength (UTS / density) 43 kN·m/kg
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | BAg-2a | BAg-33 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
BAg-2a vs BAg-33 — frequently asked
Is BAg-33 stronger than BAg-2a?
Yes. BAg-33 has a typical yield strength of 240 MPa (34.8 ksi) against 210 MPa (30.5 ksi) for BAg-2a — about 14% more. Tensile strength is 400 MPa (58 ksi) vs 400 MPa (58 ksi).
Which is cheaper, BAg-2a or BAg-33?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose BAg-2a over BAg-33?
Pick BAg-2a when the part is bent, formed or impact-loaded. Pick BAg-33 when strength drives the design, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in BAg-2a and BAg-33 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.