Precious Metal B685 1/2H vs B685-O
Precious Metal · B685 temper comparison
B685 1/2H and B685-O are two conditions of the same precious metal grade, B685: 1/2H (half hard) versus O (annealed). The chemistry is identical, so every difference below comes from the condition. B685 1/2H is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 200 MPa (29 ksi) for B685-O, about 3.1 times as much; tensile strength follows at 760 MPa (110 ksi) vs 500 MPa (72.5 ksi). In exchange, B685-O is the more ductile: elongation 30% versus 8% for B685 1/2H, and B685 1/2H is harder (225 HV vs 150 HV). B685-O runs hotter in service (450°C vs 275°C continuous).
B685 1/2HChoose it when strength drives the design.
B685-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
B685 1/2H vs B685-O: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Fatigue Strength (Endurance Limit)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 130 GPa18.9 Msi · Shear Modulus 48 GPa7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.37 · Shear Strength 300 MPa43.5 ksi · Hardness, Brinell 145 HB · Hardness, Rockwell B 78 HRB
Physical
Density and transition temperatures.
Same in both: Density 10.4 g/cm³0.38 lb/in³ · Melting Point (Solidus) 1,200°C2,192 °F · Liquidus Temperature 1,230°C2,246 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 22 W/m·K12.7 BTU/hr·ft·°F · Specific Heat Capacity 300 J/kg·K0.07 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 14 µm/m·K7.8 µin/in·°F · Latent Heat of Fusion 176 J/g75.7 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.15 V · Corrosion Resistance 92 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Formability (cold)
Same in both: Machinability 30 / 100 · Machinability Rating (AISI 1212 = 100 %) 22% · Weldability 62 / 100 · Castability 55 / 100 · Brazeability / Solderability 85 / 100 · Polishability 90 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 24,000 MJ/kg1.03×10⁷ BTU/lb · Embodied Carbon (primary production) 2,200 kg CO₂/kg · Embodied Water 90,000 L/kg10,784 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
B685 1/2H vs B685-O — frequently asked
Is B685 1/2H stronger than B685-O?
Yes. B685 1/2H has a typical yield strength of 620 MPa (89.9 ksi) against 200 MPa (29 ksi) for B685-O — about 3.1 times as much. Tensile strength is 760 MPa (110 ksi) vs 500 MPa (72.5 ksi).
Which condition does FabDigit quote by default, 1/2H or O?
O is the default B685 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose B685 1/2H over B685-O?
Pick B685 1/2H when strength drives the design. Pick B685-O when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in B685 1/2H and B685-O side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.