Precious Metal B617-H06 vs B617-O
Precious Metal · B617 temper comparison
B617-H06 and B617-O are two conditions of the same precious metal grade, B617: H06 (extra hard) versus O (annealed). The chemistry is identical, so every difference below comes from the condition. B617-H06 is the stronger of the two: yield strength 385 MPa (55.8 ksi) against 65 MPa (9.43 ksi) for B617-O, about 5.9 times as much; tensile strength follows at 450 MPa (65.3 ksi) vs 265 MPa (38.4 ksi). In exchange, B617-O is the more ductile: elongation 40% versus 6% for B617-H06, and B617-H06 is harder (112 HB vs 58 HB). B617-O runs hotter in service (200°C vs 145°C continuous). On the shop floor, B617-H06 machines more easily (66 vs 55 out of 100).
B617-H06Choose it when strength drives the design, or when the part is machined in volume.
B617-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
B617-H06 vs B617-O: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 79 GPa11.5 Msi · Shear Modulus 29 GPa4.2 Msi · Bulk Modulus 100 GPa14.5 Msi · Poisson's Ratio 0.37 · Reduction in Area 70%
Physical
Density and transition temperatures.
Same in both: Density 10.31 g/cm³0.37 lb/in³ · Melting Point (Solidus) 779°C1,434 °F · Liquidus Temperature 875°C1,607 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 237 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.7 µm/m·K10.4 µin/in·°F · Latent Heat of Fusion 105 J/g45.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 2.03×10⁻⁸ Ω·m0.799 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.05 V · Corrosion Resistance 78 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 55% · Weldability 55 / 100 · Castability 72 / 100 · Brazeability / Solderability 95 / 100 · Polishability 95 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,500 MJ/kg644,885 BTU/lb · Embodied Carbon (primary production) 100 kg CO₂/kg · Embodied Water 3,000 L/kg359 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
B617-H06 vs B617-O — frequently asked
Is B617-H06 stronger than B617-O?
Yes. B617-H06 has a typical yield strength of 385 MPa (55.8 ksi) against 65 MPa (9.43 ksi) for B617-O — about 5.9 times as much. Tensile strength is 450 MPa (65.3 ksi) vs 265 MPa (38.4 ksi).
Which condition does FabDigit quote by default, H06 or O?
O is the default B617 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, B617-H06 or B617-O?
B617-H06, by a small margin. Both rate good for machinability — 66/100 against 55/100 for B617-O.
Ready to make it?
Upload a CAD file and FabDigit prices the part in B617-H06 and B617-O side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.