Precious Metal 86.5Ag-13.5CdO-H01 vs 86.5Ag-13.5CdO-H02
Precious Metal · 86.5Ag-13.5CdO temper comparison
86.5Ag-13.5CdO-H01 and 86.5Ag-13.5CdO-H02 are two conditions of the same precious metal grade, 86.5Ag-13.5CdO: H01 (quarter hard) versus H02 (half hard). The chemistry is identical, so every difference below comes from the condition. 86.5Ag-13.5CdO-H02 is the stronger of the two: yield strength 220 MPa (31.9 ksi) against 175 MPa (25.4 ksi) for 86.5Ag-13.5CdO-H01, about 26% more; tensile strength follows at 295 MPa (42.8 ksi) vs 265 MPa (38.4 ksi). In exchange, 86.5Ag-13.5CdO-H01 is the more ductile: elongation 10% versus 6% for 86.5Ag-13.5CdO-H02, and 86.5Ag-13.5CdO-H02 is harder (80 HB vs 71 HB). 86.5Ag-13.5CdO-H01 runs hotter in service (230°C vs 210°C continuous).
86.5Ag-13.5CdO-H01Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
86.5Ag-13.5CdO-H02Choose it when strength drives the design.
86.5Ag-13.5CdO-H01 vs 86.5Ag-13.5CdO-H02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
86.5Ag-13.5CdO-H0186.5Ag-13.5CdO-H02
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 82 GPa11.9 Msi · Shear Modulus 30 GPa4.4 Msi · Bulk Modulus 103 GPa14.9 Msi · Poisson's Ratio 0.37
Physical
Density and transition temperatures.
Same in both: Density 10.1 g/cm³0.36 lb/in³ · Melting Point (Solidus) 960°C1,760 °F · Liquidus Temperature 962°C1,764 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 240 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.5 µm/m·K10.3 µin/in·°F · Latent Heat of Fusion 92 J/g39.6 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0 V · Corrosion Resistance 82 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 55% · Weldability 70 / 100 · Castability 40 / 100 · Brazeability / Solderability 60 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,450 MJ/kg623,388 BTU/lb · Embodied Carbon (primary production) 105 kg CO₂/kg · Embodied Water 2,200 L/kg264 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
86.5Ag-13.5CdO-H01 vs 86.5Ag-13.5CdO-H02 — frequently asked
Is 86.5Ag-13.5CdO-H02 stronger than 86.5Ag-13.5CdO-H01?
Yes. 86.5Ag-13.5CdO-H02 has a typical yield strength of 220 MPa (31.9 ksi) against 175 MPa (25.4 ksi) for 86.5Ag-13.5CdO-H01 — about 26% more. Tensile strength is 295 MPa (42.8 ksi) vs 265 MPa (38.4 ksi).
Which condition does FabDigit quote by default, H01 or H02?
O is the default 86.5Ag-13.5CdO condition in the FabDigit quote flow (neither H01 nor H02). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 86.5Ag-13.5CdO-H01 or 86.5Ag-13.5CdO-H02?
86.5Ag-13.5CdO-H02. Its machinability rates good (55/100) against fair (50/100) for 86.5Ag-13.5CdO-H01.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 86.5Ag-13.5CdO-H01 and 86.5Ag-13.5CdO-H02 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.