Precious Metal 85Ag-15Ni-H01 vs 85Ag-15Ni-H04
Precious Metal · 85Ag-15Ni temper comparison
85Ag-15Ni-H01 and 85Ag-15Ni-H04 are two conditions of the same precious metal grade, 85Ag-15Ni: H01 (quarter hard) versus H04 (full hard). The chemistry is identical, so every difference below comes from the condition. 85Ag-15Ni-H04 is the stronger of the two: yield strength 315 MPa (45.7 ksi) against 190 MPa (27.6 ksi) for 85Ag-15Ni-H01, about 66% more; tensile strength follows at 350 MPa (50.8 ksi) vs 270 MPa (39.2 ksi). In exchange, 85Ag-15Ni-H01 is the more ductile: elongation 13% versus 3% for 85Ag-15Ni-H04, and 85Ag-15Ni-H04 is harder (95 HB vs 71 HB). 85Ag-15Ni-H01 runs hotter in service (200°C vs 180°C continuous).
85Ag-15Ni-H01Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
85Ag-15Ni-H04Choose it when strength drives the design.
85Ag-15Ni-H01 vs 85Ag-15Ni-H04: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 100 GPa14.5 Msi · Shear Modulus 37 GPa5.4 Msi · Bulk Modulus 118 GPa17.1 Msi · Poisson's Ratio 0.36
Physical
Density and transition temperatures.
Same in both: Density 10.1 g/cm³0.36 lb/in³ · Melting Point (Solidus) 961°C1,762 °F · Liquidus Temperature 1,455°C2,651 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 265 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.5 µm/m·K10.3 µin/in·°F · Latent Heat of Fusion 118 J/g50.7 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0 V · Corrosion Resistance 82 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 30% · Weldability 55 / 100 · Castability 10 / 100 · Brazeability / Solderability 90 / 100 · Polishability 82 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 1,300 MJ/kg558,900 BTU/lb · Embodied Carbon (primary production) 110 kg CO₂/kg · Embodied Water 2,500 L/kg300 gal/lb · Typical Recycled Content 50%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
85Ag-15Ni-H01 vs 85Ag-15Ni-H04 — frequently asked
Is 85Ag-15Ni-H04 stronger than 85Ag-15Ni-H01?
Yes. 85Ag-15Ni-H04 has a typical yield strength of 315 MPa (45.7 ksi) against 190 MPa (27.6 ksi) for 85Ag-15Ni-H01 — about 66% more. Tensile strength is 350 MPa (50.8 ksi) vs 270 MPa (39.2 ksi).
Which condition does FabDigit quote by default, H01 or H04?
O is the default 85Ag-15Ni condition in the FabDigit quote flow (neither H01 nor H04). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 85Ag-15Ni-H01 or 85Ag-15Ni-H04?
85Ag-15Ni-H04, by a small margin. Both rate fair for machinability — 50/100 against 42/100 for 85Ag-15Ni-H01.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 85Ag-15Ni-H01 and 85Ag-15Ni-H04 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.