Precious Metal 14K-ANN vs 14K-H02
Precious Metal · 14K temper comparison
14K-ANN and 14K-H02 are two conditions of the same precious metal grade, 14K: ANN (annealed) versus H02 (half hard). The chemistry is identical, so every difference below comes from the condition. 14K-H02 is the stronger of the two: yield strength 470 MPa (68.2 ksi) against 220 MPa (31.9 ksi) for 14K-ANN, about 114% more; tensile strength follows at 600 MPa (87 ksi) vs 400 MPa (58 ksi). In exchange, 14K-ANN is the more ductile: elongation 35% versus 10% for 14K-H02, and 14K-H02 is harder (176 HB vs 133 HB). 14K-ANN runs hotter in service (250°C vs 180°C continuous). On the shop floor, 14K-H02 machines more easily (very good vs good).
14K-ANNChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
14K-H02Choose it when strength drives the design, or when the part is machined in volume.
14K-ANN vs 14K-H02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 80 GPa11.6 Msi · Shear Modulus 30 GPa4.4 Msi · Bulk Modulus 105 GPa15.2 Msi · Poisson's Ratio 0.35
Physical
Density and transition temperatures.
Same in both: Density 13.07 g/cm³0.47 lb/in³ · Melting Point (Solidus) 802°C1,476 °F · Liquidus Temperature 830°C1,526 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 295 J/kg·K0.07 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 14.5 µm/m·K8.1 µin/in·°F · Latent Heat of Fusion 95 J/g40.8 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) 0.25 V · Corrosion Resistance 85 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 85 / 100 · Brazeability / Solderability 92 / 100 · Polishability 95 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 150,000 MJ/kg6.45×10⁷ BTU/lb · Embodied Carbon (primary production) 10,000 kg CO₂/kg · Embodied Water 140,000 L/kg16,776 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
14K-ANN vs 14K-H02 — frequently asked
Is 14K-H02 stronger than 14K-ANN?
Yes. 14K-H02 has a typical yield strength of 470 MPa (68.2 ksi) against 220 MPa (31.9 ksi) for 14K-ANN — about 114% more. Tensile strength is 600 MPa (87 ksi) vs 400 MPa (58 ksi).
Which condition does FabDigit quote by default, ANN or H02?
ANN is the default 14K condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 14K-ANN or 14K-H02?
14K-H02. Its machinability rates very good (70/100) against good (55/100) for 14K-ANN; for welding the order is 14K-ANN first (very good, 80/100) then 14K-H02 (very good, 72/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 14K-ANN and 14K-H02 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.