TP-PI GF30 vs TP-PI GR15-PTFE10
Polymer · TP-PI grade comparison
TP-PI GF30 and TP-PI GR15-PTFE10 are two grades of the same polymer grade, TP-PI: GF30 (30 % glass-fiber reinforced) versus GR15-PTFE10. The chemistry is identical, so every difference below comes from the condition. TP-PI GF30 is the stronger of the two: tensile strength 165 MPa (23.9 ksi) against 52 MPa (7.54 ksi) for TP-PI GR15-PTFE10, about 3.2 times as much. In exchange, TP-PI GR15-PTFE10 is the more ductile: elongation 4% versus 3% for TP-PI GF30. TP-PI GF30 is stiffer (9.5 GPa vs 3.8 GPa) and TP-PI GF30 runs hotter in service (250°C vs 230°C continuous). On the shop floor, TP-PI GR15-PTFE10 machines more easily (good vs fair).
TP-PI GF30Choose it when strength drives the design, or when the part sees heat.
TP-PI GR15-PTFE10Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
TP-PI GF30 vs TP-PI GR15-PTFE10: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Shear Strength
Izod Impact, Notched
Hardness, Rockwell M
Same in both: Shear Modulus 1.1 GPa0.15 Msi · Bulk Modulus 4 GPa0.58 Msi · Poisson's Ratio 0.38 · Yield Strength (0.2% offset) 90 MPa13.1 ksi · Compressive Modulus 2.8 GPa0.41 Msi · Fracture Toughness (K_IC) 3 MPa·√m2.7 ksi·√in · Hardness, Shore D 88 Shore D · Hardness, Rockwell R 125 HRR
Physical
Density and transition temperatures.
Same in both: Density 1.55 g/cm³0.06 lb/in³ · Melting Temperature (Tm) 388°C730 °F · Glass Transition (Tg) 250°C482 °F · Water Absorption (24 h) 0.24% · Water Absorption (Saturation) 1.2% · Refractive Index 1.7
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Limiting Oxygen Index
Same in both: Specific Heat Capacity 1,100 J/kg·K0.26 BTU/lb·°F · Min Service Temperature -269°C-452 °F · Vicat Softening Point (B50) 255°C491 °F · Max Service Temperature (short-term) 300°C572 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹⁴ Ω·m3.94×10²¹ µΩ·in · Dielectric Strength 22 kV/mm559 V/mil · Dielectric Constant (1 MHz) 3.2 · Dissipation Factor (1 MHz) 0.002 · Volume Resistivity 1×10¹⁶ Ω·cm · Surface Resistivity 1×10¹⁶ Ω · Comparative Tracking Index (CTI) 175 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: UV / Weathering Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Mold Shrinkage
Same in both: Weldability 25 / 100 · Formability (cold) 25 / 100 · Polishability 60 / 100 · Melt Flow Rate 3 g/10 min · Processing Melt Temperature (typ.) 410°C770 °F · Mold Temperature (typ.) 200°C392 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 300 MJ/kg128,977 BTU/lb · Embodied Carbon (primary production) 15 kg CO₂/kg · Embodied Water 500 L/kg59.9 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
TP-PI GF30 vs TP-PI GR15-PTFE10 — frequently asked
Is TP-PI GF30 stronger than TP-PI GR15-PTFE10?
Yes. TP-PI GF30 has a typical tensile strength of 165 MPa (23.9 ksi) against 52 MPa (7.54 ksi) for TP-PI GR15-PTFE10 — about 3.2 times as much.
Which grade does FabDigit quote by default, GF30 or GR15-PTFE10?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, TP-PI GF30 or TP-PI GR15-PTFE10?
TP-PI GR15-PTFE10. Its machinability rates good (68/100) against fair (42/100) for TP-PI GF30.
Ready to make it?
Upload a CAD file and FabDigit prices the part in TP-PI GF30 and TP-PI GR15-PTFE10 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.