PESU-GF30 GF30 vs PESU-GF30 GF30-PTFE
Polymer · PESU-GF30 grade comparison
PESU-GF30 GF30 and PESU-GF30 GF30-PTFE are two grades of the same polymer grade, PESU-GF30: GF30 (standard 30 % glass-fiber reinforced injection-molding grade) versus GF30-PTFE. The chemistry is identical, so every difference below comes from the condition. PESU-GF30 GF30 is the stronger of the two: tensile strength 150 MPa (21.8 ksi) against 115 MPa (16.7 ksi) for PESU-GF30 GF30-PTFE, about 30% more. PESU-GF30 GF30 is the more ductile: elongation 2.5% versus 2% for PESU-GF30 GF30-PTFE. PESU-GF30 GF30 is lighter (1.6 g/cm³ vs 1.68 g/cm³ for PESU-GF30 GF30-PTFE) and PESU-GF30 GF30 is stiffer (9.5 GPa vs 8.5 GPa). On the shop floor, PESU-GF30 GF30 welds better (fair vs poor).
PESU-GF30 GF30Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
PESU-GF30 GF30 vs PESU-GF30 GF30-PTFE: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
PESU-GF30 GF30PESU-GF30 GF30-PTFE
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Shear Strength
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Same in both: Shear Modulus 3.4 GPa0.49 Msi · Bulk Modulus 14 GPa2 Msi · Poisson's Ratio 0.39 · Compressive Modulus 8.5 GPa1.2 Msi
Physical
Density and transition temperatures.
Density
Same in both: Glass Transition (Tg) 222°C432 °F · Water Absorption (24 h) 0.43% · Water Absorption (Saturation) 1.6%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Same in both: Specific Heat Capacity 1,100 J/kg·K0.26 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 22 µm/m·K12.2 µin/in·°F · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -50°C-58 °F · Max Service Temperature (short-term) 250°C482 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹³ Ω·m3.94×10²⁰ µΩ·in · Dielectric Strength 22 kV/mm559 V/mil · Dielectric Constant (1 MHz) 3.9 · Dissipation Factor (1 MHz) 0.009 · Volume Resistivity 1×10¹⁵ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 150 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: UV / Weathering Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Same in both: Formability (cold) 10 / 100 · Polishability 30 / 100 · Mold Shrinkage 0.3% · Melt Flow Rate 20 g/10 min · Processing Melt Temperature (typ.) 360°C680 °F · Mold Temperature (typ.) 160°C320 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 120 MJ/kg51,591 BTU/lb · Embodied Carbon (primary production) 7.5 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PESU-GF30 GF30 vs PESU-GF30 GF30-PTFE — frequently asked
Is PESU-GF30 GF30 stronger than PESU-GF30 GF30-PTFE?
Yes. PESU-GF30 GF30 has a typical tensile strength of 150 MPa (21.8 ksi) against 115 MPa (16.7 ksi) for PESU-GF30 GF30-PTFE — about 30% more.
Which grade does FabDigit quote by default, GF30 or GF30-PTFE?
GF30 is the default PESU-GF30 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, PESU-GF30 GF30 or PESU-GF30 GF30-PTFE?
PESU-GF30 GF30-PTFE, by a small margin. Both rate fair for machinability — 50/100 against 45/100 for PESU-GF30 GF30; for welding the order is PESU-GF30 GF30 first (fair, 50/100) then PESU-GF30 GF30-PTFE (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in PESU-GF30 GF30 and PESU-GF30 GF30-PTFE side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.