PC-Medical GF10 vs PC-Medical GF20
Polymer · PC-Medical grade comparison
PC-Medical GF10 and PC-Medical GF20 are two grades of the same polymer grade, PC-Medical: GF10 (10% glass-fiber reinforced medical PC) versus GF20 (20% glass-fiber reinforced medical PC). The chemistry is identical, so every difference below comes from the condition. PC-Medical GF20 is the stronger of the two: tensile strength 105 MPa (15.2 ksi) against 85 MPa (12.3 ksi) for PC-Medical GF10, about 24% more. In exchange, PC-Medical GF10 is the more ductile: elongation 6% versus 4% for PC-Medical GF20. PC-Medical GF10 is lighter (1.27 g/cm³ vs 1.34 g/cm³ for PC-Medical GF20) and PC-Medical GF20 is stiffer (5 GPa vs 3.6 GPa).
PC-Medical GF10Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PC-Medical GF20Choose it when strength drives the design.
PC-Medical GF10 vs PC-Medical GF20: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
PC-Medical GF10PC-Medical GF20
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Same in both: Shear Modulus 0.85 GPa0.12 Msi · Bulk Modulus 3 GPa0.49 Msi · Poisson's Ratio 0.37 · Yield Strength (0.2% offset) 62 MPa9 ksi · Compressive Strength 80 MPa11.6 ksi · Compressive Modulus 2.4 GPa0.35 Msi · Shear Strength 40 MPa5.8 ksi · Fracture Toughness (K_IC) 2.7 MPa·√m2.5 ksi·√in · Hardness, Shore D 82 Shore D · Hardness, Rockwell M 72 HRM · Hardness, Rockwell R 120 HRR
Physical
Density and transition temperatures.
Density
Same in both: Glass Transition (Tg) 147°C297 °F · Water Absorption (24 h) 0.15% · Water Absorption (Saturation) 0.35% · Refractive Index 1.586 · Light Transmission 0%
Thermal
How each material carries heat and how hot it can run.
Thermal Expansion (CTE, 20–100 °C)
Heat Deflection Temp. @ 1.8 MPa
Same in both: Thermal Conductivity 0.2 W/m·K0.12 BTU/hr·ft·°F · Specific Heat Capacity 1,200 J/kg·K0.29 BTU/lb·°F · Max Service Temperature (continuous) 115°C239 °F · Min Service Temperature -40°C-40 °F · Heat Deflection Temp. @ 0.45 MPa 138°C280 °F · Vicat Softening Point (B50) 146°C295 °F · Limiting Oxygen Index 26% · Max Service Temperature (short-term) 145°C293 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹⁴ Ω·m3.94×10²¹ µΩ·in · Dielectric Strength 25 kV/mm635 V/mil · Dielectric Constant (1 MHz) 2.9 · Dissipation Factor (1 MHz) 0.01 · Volume Resistivity 1×10¹⁶ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 250 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 70 / 100 · UV / Weathering Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Mold Shrinkage
Same in both: Weldability 75 / 100 · Formability (cold) 70 / 100 · Polishability 90 / 100 · Melt Flow Rate 10 g/10 min · Processing Melt Temperature (typ.) 300°C572 °F · Mold Temperature (typ.) 95°C203 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 105 MJ/kg45,142 BTU/lb · Embodied Carbon (primary production) 6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PC-Medical GF10 vs PC-Medical GF20 — frequently asked
Is PC-Medical GF20 stronger than PC-Medical GF10?
Yes. PC-Medical GF20 has a typical tensile strength of 105 MPa (15.2 ksi) against 85 MPa (12.3 ksi) for PC-Medical GF10 — about 24% more.
Which grade does FabDigit quote by default, GF10 or GF20?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, PC-Medical GF10 or PC-Medical GF20?
PC-Medical GF10, by a small margin. Both rate fair for machinability — 50/100 against 45/100 for PC-Medical GF20.