PC-HT GF20 vs PC-HT GF30
Polymer · PC-HT grade comparison
PC-HT GF20 and PC-HT GF30 are two grades of the same polymer grade, PC-HT: GF20 (20% glass-fiber reinforced) versus GF30 (30% glass-fiber reinforced). The chemistry is identical, so every difference below comes from the condition. PC-HT GF30 is the stronger of the two: tensile strength 130 MPa (18.9 ksi) against 110 MPa (16 ksi) for PC-HT GF20, about 18% more. In exchange, PC-HT GF20 is the more ductile: elongation 4% versus 3% for PC-HT GF30. PC-HT GF20 is lighter (1.35 g/cm³ vs 1.43 g/cm³ for PC-HT GF30) and PC-HT GF30 is stiffer (8.5 GPa vs 6 GPa).
PC-HT GF20Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PC-HT GF30Choose it when strength drives the design.
PC-HT GF20 vs PC-HT GF30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Same in both: Shear Modulus 0.87 GPa0.13 Msi · Bulk Modulus 4 GPa0.51 Msi · Poisson's Ratio 0.38 · Yield Strength (0.2% offset) 68 MPa9.9 ksi · Compressive Strength 85 MPa12.3 ksi · Compressive Modulus 2.4 GPa0.35 Msi · Shear Strength 62 MPa9 ksi · Fracture Toughness (K_IC) 3 MPa·√m2.7 ksi·√in · Hardness, Shore D 84 Shore D · Hardness, Rockwell M 76 HRM · Hardness, Rockwell R 120 HRR
Physical
Density and transition temperatures.
Density
Same in both: Glass Transition (Tg) 185°C365 °F · Water Absorption (24 h) 0.2% · Water Absorption (Saturation) 0.35% · Refractive Index 1.59 · Light Transmission 87%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Heat Deflection Temp. @ 1.8 MPa
Same in both: Specific Heat Capacity 1,200 J/kg·K0.29 BTU/lb·°F · Max Service Temperature (continuous) 140°C284 °F · Min Service Temperature -40°C-40 °F · Heat Deflection Temp. @ 0.45 MPa 172°C342 °F · Vicat Softening Point (B50) 178°C352 °F · Limiting Oxygen Index 27% · Max Service Temperature (short-term) 170°C338 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹⁴ Ω·m3.94×10²¹ µΩ·in · Dielectric Strength 28 kV/mm711 V/mil · Dielectric Constant (1 MHz) 2.95 · Dissipation Factor (1 MHz) 0.01 · Volume Resistivity 1×10¹⁶ Ω·cm · Surface Resistivity 1×10¹⁶ Ω · Comparative Tracking Index (CTI) 250 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 70 / 100 · UV / Weathering Resistance 35 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Mold Shrinkage
Same in both: Weldability 70 / 100 · Formability (cold) 65 / 100 · Polishability 85 / 100 · Melt Flow Rate 6 g/10 min · Processing Melt Temperature (typ.) 325°C617 °F · Mold Temperature (typ.) 115°C239 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 112 MJ/kg48,151 BTU/lb · Embodied Carbon (primary production) 7 kg CO₂/kg · Embodied Water 260 L/kg31.2 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PC-HT GF20 vs PC-HT GF30 — frequently asked
Is PC-HT GF30 stronger than PC-HT GF20?
Yes. PC-HT GF30 has a typical tensile strength of 130 MPa (18.9 ksi) against 110 MPa (16 ksi) for PC-HT GF20 — about 18% more.
Which grade does FabDigit quote by default, GF20 or GF30?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, PC-HT GF20 or PC-HT GF30?
PC-HT GF20, by a small margin. Both rate fair for machinability — 52/100 against 45/100 for PC-HT GF30.