PBT-GF30 GF30 vs PBT-GF30 GF30-HFFR
Polymer · PBT-GF30 grade comparison
PBT-GF30 GF30 and PBT-GF30 GF30-HFFR are two grades of the same polymer grade, PBT-GF30: GF30 (30% glass fiber, natural / uncolored, unmodified) versus GF30-HFFR (GF30 halogen-free FR). The chemistry is identical, so every difference below comes from the condition. PBT-GF30 GF30 is the stronger of the two: tensile strength 130 MPa (18.9 ksi) against 110 MPa (16 ksi) for PBT-GF30 GF30-HFFR, about 18% more. PBT-GF30 GF30 is the more ductile: elongation 3% versus 2.2% for PBT-GF30 GF30-HFFR. PBT-GF30 GF30 is lighter (1.53 g/cm³ vs 1.6 g/cm³ for PBT-GF30 GF30-HFFR) and PBT-GF30 GF30 is stiffer (10 GPa vs 9.5 GPa). On the shop floor, PBT-GF30 GF30 welds better (45 vs 35 out of 100).
PBT-GF30 GF30Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
PBT-GF30 GF30 vs PBT-GF30 GF30-HFFR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
PBT-GF30 GF30PBT-GF30 GF30-HFFR
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Hardness, Rockwell R
Same in both: Shear Modulus 3.6 GPa0.52 Msi · Poisson's Ratio 0.38 · Compressive Modulus 8.5 GPa1.2 Msi · Flexural Modulus 9 GPa1.3 Msi
Physical
Density and transition temperatures.
Density
Same in both: Melting Temperature (Tm) 225°C437 °F · Glass Transition (Tg) 50°C122 °F · Water Absorption (24 h) 0.06% · Water Absorption (Saturation) 0.35%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Limiting Oxygen Index
Same in both: Specific Heat Capacity 1,400 J/kg·K0.33 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 25 µm/m·K13.9 µin/in·°F · Max Service Temperature (continuous) 130°C266 °F · Min Service Temperature -40°C-40 °F · Vicat Softening Point (B50) 200°C392 °F · Max Service Temperature (short-term) 190°C374 °F
Electrical
Conductivity and insulation.
Comparative Tracking Index (CTI)
Same in both: Electrical Resistivity 1×10¹⁴ Ω·m3.94×10²¹ µΩ·in · Dielectric Strength 30 kV/mm762 V/mil · Dielectric Constant (1 MHz) 3.7 · Dissipation Factor (1 MHz) 0.02 · Volume Resistivity 1×10¹⁶ Ω·cm · Surface Resistivity 1×10¹⁵ Ω
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: UV / Weathering Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Melt Flow Rate
Same in both: Machinability 55 / 100 · Polishability 30 / 100 · Mold Shrinkage 0.4% · Processing Melt Temperature (typ.) 260°C500 °F · Mold Temperature (typ.) 80°C176 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 85 MJ/kg36,543 BTU/lb · Embodied Carbon (primary production) 4.4 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 5%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PBT-GF30 GF30 vs PBT-GF30 GF30-HFFR — frequently asked
Is PBT-GF30 GF30 stronger than PBT-GF30 GF30-HFFR?
Yes. PBT-GF30 GF30 has a typical tensile strength of 130 MPa (18.9 ksi) against 110 MPa (16 ksi) for PBT-GF30 GF30-HFFR — about 18% more.
Which grade does FabDigit quote by default, GF30 or GF30-HFFR?
GF30 is the default PBT-GF30 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, PBT-GF30 GF30 or PBT-GF30 GF30-HFFR?
PBT-GF30 GF30. Its weldability rates fair (45/100) against fair (35/100) for PBT-GF30 GF30-HFFR.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PBT-GF30 GF30 and PBT-GF30 GF30-HFFR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.