PAR BLEND-PET vs PAR GF30
Polymer · PAR grade comparison
PAR BLEND-PET and PAR GF30 are two grades of the same polymer grade, PAR: BLEND-PET (pAR/polyester alloy) versus GF30 (30 % glass-fiber reinforced). The chemistry is identical, so every difference below comes from the condition. PAR GF30 is the stronger of the two: yield strength 68 MPa (9.86 ksi) against 60 MPa (8.7 ksi) for PAR BLEND-PET, about 13% more; tensile strength follows at 120 MPa (17.4 ksi) vs 65 MPa (9.43 ksi). In exchange, PAR BLEND-PET is the more ductile: elongation 30% versus 2.5% for PAR GF30. PAR BLEND-PET is lighter (1.3 g/cm³ vs 1.45 g/cm³ for PAR GF30) and PAR GF30 is stiffer (8.5 GPa vs 2.4 GPa). On the shop floor, PAR BLEND-PET machines more easily (good vs fair) and PAR GF30 welds better (good vs fair).
PAR BLEND-PETChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PAR GF30Choose it when strength drives the design, or when the part sees heat.
PAR BLEND-PET vs PAR GF30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Shear Strength
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Hardness, Rockwell R
Same in both: Shear Modulus 0.75 GPa0.11 Msi · Bulk Modulus 4 GPa0.51 Msi · Poisson's Ratio 0.4 · Compressive Modulus 2.2 GPa0.32 Msi
Physical
Density and transition temperatures.
Density
Light Transmission
Same in both: Glass Transition (Tg) 190°C374 °F · Water Absorption (24 h) 0.26% · Water Absorption (Saturation) 0.8% · Refractive Index 1.61
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Same in both: Specific Heat Capacity 1,200 J/kg·K0.29 BTU/lb·°F · Min Service Temperature -50°C-58 °F · Max Service Temperature (short-term) 180°C356 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹⁴ Ω·m3.94×10²¹ µΩ·in · Dielectric Strength 20 kV/mm508 V/mil · Dielectric Constant (1 MHz) 3 · Dissipation Factor (1 MHz) 0.012 · Volume Resistivity 1×10¹⁶ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 200 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: UV / Weathering Resistance 90 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Mold Shrinkage
Processing Melt Temperature (typ.)
Same in both: Polishability 75 / 100 · Mold Temperature (typ.) 130°C266 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 145 MJ/kg62,339 BTU/lb · Embodied Carbon (primary production) 7.5 kg CO₂/kg · Embodied Water 350 L/kg41.9 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PAR BLEND-PET vs PAR GF30 — frequently asked
Is PAR GF30 stronger than PAR BLEND-PET?
Yes. PAR GF30 has a typical yield strength of 68 MPa (9.86 ksi) against 60 MPa (8.7 ksi) for PAR BLEND-PET — about 13% more. Tensile strength is 120 MPa (17.4 ksi) vs 65 MPa (9.43 ksi).
Which grade does FabDigit quote by default, BLEND-PET or GF30?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, PAR BLEND-PET or PAR GF30?
PAR BLEND-PET. Its machinability rates good (62/100) against fair (42/100) for PAR GF30; for welding the order is PAR GF30 first (good, 60/100) then PAR BLEND-PET (fair, 50/100).