PA10T COPO vs PA10T GF30
Polymer · PA10T grade comparison
PA10T COPO and PA10T GF30 are two grades of the same polymer grade, PA10T: COPO (PA10T copolymer) versus GF30 (30 % glass-fiber reinforced). The chemistry is identical, so every difference below comes from the condition. PA10T GF30 is the stronger of the two: yield strength 90 MPa (13.1 ksi) against 85 MPa (12.3 ksi) for PA10T COPO, about 6% more; tensile strength follows at 190 MPa (27.6 ksi) vs 90 MPa (13.1 ksi). In exchange, PA10T COPO is the more ductile: elongation 35% versus 2.5% for PA10T GF30. PA10T COPO is lighter (1.11 g/cm³ vs 1.35 g/cm³ for PA10T GF30) and PA10T GF30 is stiffer (10 GPa vs 2.6 GPa). On the shop floor, PA10T COPO machines more easily (good vs fair).
PA10T COPOChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PA10T GF30Choose it when strength drives the design, or when the part sees heat.
PA10T COPO vs PA10T GF30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Same in both: Poisson's Ratio 0.4
Physical
Density and transition temperatures.
Density
Melting Temperature (Tm)
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Max Service Temperature (short-term)
Same in both: Specific Heat Capacity 1,500 J/kg·K0.36 BTU/lb·°F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 1×10¹³ Ω·m3.94×10²⁰ µΩ·in · Dielectric Strength 28 kV/mm711 V/mil · Dielectric Constant (1 MHz) 3.6 · Dissipation Factor (1 MHz) 0.02 · Volume Resistivity 1×10¹⁵ Ω·cm · Surface Resistivity 1×10¹⁵ Ω · Comparative Tracking Index (CTI) 600 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 80 / 100 · UV / Weathering Resistance 40 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Mold Shrinkage
Processing Melt Temperature (typ.)
Same in both: Polishability 55 / 100 · Mold Temperature (typ.) 135°C275 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 100 MJ/kg42,992 BTU/lb · Embodied Carbon (primary production) 5 kg CO₂/kg · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PA10T COPO vs PA10T GF30 — frequently asked
Is PA10T GF30 stronger than PA10T COPO?
Yes. PA10T GF30 has a typical yield strength of 90 MPa (13.1 ksi) against 85 MPa (12.3 ksi) for PA10T COPO — about 6% more. Tensile strength is 190 MPa (27.6 ksi) vs 90 MPa (13.1 ksi).
Which grade does FabDigit quote by default, COPO or GF30?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, PA10T COPO or PA10T GF30?
PA10T COPO. Its machinability rates good (62/100) against fair (40/100) for PA10T GF30; for welding the order is PA10T COPO first (good, 60/100) then PA10T GF30 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in PA10T COPO and PA10T GF30 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.