GB/T 10801.1 Type II vs JIS A9511 EPS
Polymer · grade comparison
GB/T 10801.1 Type II and JIS A9511 EPS are both polymer grades. GB/T 10801.1 Type II is the stronger of the two: tensile strength 0.25 MPa (0.0363 ksi) against 0.2 MPa (0.029 ksi) for JIS A9511 EPS, about 25% more. GB/T 10801.1 Type II is the more ductile: elongation 6% versus 1.5% for JIS A9511 EPS. JIS A9511 EPS is lighter (0.02 g/cm³ vs 0.02 g/cm³ for GB/T 10801.1 Type II) and JIS A9511 EPS is stiffer (0.01 GPa vs 0 GPa).
GB/T 10801.1 Type IIChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
JIS A9511 EPSChoose it when weight is the constraint.
GB/T 10801.1 Type II vs JIS A9511 EPS: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
GB/T 10801.1 Type IIJIS A9511 EPS
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Shear Strength
Yield Strength (0.2% offset)
Flexural Modulus
Compression Set (22 h, 70 °C)
Same in both: Poisson's Ratio 0.1
Physical
Density and transition temperatures.
Density
Water Absorption (Saturation)
Water Absorption (24 h)
Same in both: Glass Transition (Tg) 100°C212 °F
Thermal
How each material carries heat and how hot it can run.
Min Service Temperature
Vicat Softening Point (B50)
Limiting Oxygen Index
Same in both: Thermal Conductivity 0.04 W/m·K0.02 BTU/hr·ft·°F · Specific Heat Capacity 1,400 J/kg·K0.33 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 65 µm/m·K36.1 µin/in·°F · Max Service Temperature (continuous) 75°C167 °F · Max Service Temperature (short-term) 85°C185 °F
Electrical
Conductivity and insulation.
Dielectric Constant (1 MHz)
Volume Resistivity
Electrical Resistivity
Dissipation Factor (1 MHz)
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Same in both: Machinability 90 / 100 · Mold Shrinkage 0.45%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 5%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | GB/T 10801.1 Type II | JIS A9511 EPS |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$ Standard | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
GB/T 10801.1 Type II vs JIS A9511 EPS — frequently asked
Is GB/T 10801.1 Type II stronger than JIS A9511 EPS?
Yes. GB/T 10801.1 Type II has a typical tensile strength of 0.25 MPa (0.0363 ksi) against 0.2 MPa (0.029 ksi) for JIS A9511 EPS — about 25% more.
Which is cheaper, GB/T 10801.1 Type II or JIS A9511 EPS?
Both sit in the same relative cost tier ($$, standard); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, GB/T 10801.1 Type II or JIS A9511 EPS?
JIS A9511 EPS. Its weldability rates poor (30/100) against poor (25/100) for GB/T 10801.1 Type II.