Dental Surgical Guide Resin vs Formlabs Rigid 10K
Polymer · grade comparison
Dental Surgical Guide Resin and Rigid 10K are both polymer grades. Rigid 10K is the stronger of the two: tensile strength 75 MPa (10.9 ksi) against 55 MPa (7.98 ksi) for Dental Surgical Guide Resin, about 36% more. In exchange, Dental Surgical Guide Resin is the more ductile: elongation 6% versus 2.5% for Rigid 10K. Dental Surgical Guide Resin is lighter (1.15 g/cm³ vs 1.55 g/cm³ for Rigid 10K) and Rigid 10K is stiffer (5.5 GPa vs 2.2 GPa). On the shop floor, Dental Surgical Guide Resin machines more easily (good vs fair) and Rigid 10K sits in a lower cost tier (premium, $$$) than Dental Surgical Guide Resin (high, $$$$).
Dental Surgical Guide ResinChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
Rigid 10KChoose it when strength drives the design, or when the part sees heat.
Dental Surgical Guide Resin vs Rigid 10K: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Dental Surgical Guide ResinRigid 10K
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Rockwell M
Same in both: Poisson's Ratio 0.35 · Hardness, Shore D 85 Shore D
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Refractive Index
Light Transmission
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Limiting Oxygen Index
Max Service Temperature (short-term)
Electrical
Conductivity and insulation.
Dielectric Constant (1 MHz)
Electrical Resistivity
Dielectric Strength
Dissipation Factor (1 MHz)
Surface Resistivity
Same in both: Volume Resistivity 1×10¹⁴ Ω·cm
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
UV / Weathering Resistance
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Mold Shrinkage
Weldability
Formability (cold)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Specific Strength (UTS / density) 48 kN·m/kg · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Dental Surgical Guide Resin | Rigid 10K |
|---|---|---|
| Injection molding | — | Yes |
| 3D printing | — | Yes |
| Default condition | — | Glass Filled |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Chrome Plating (Plastic) | — | Yes |
| Conductive Coating | — | Yes |
| Dyeing (Nylon) | — | Yes |
| EMI Shielding Coating | — | Yes |
| Painting | — | Yes |
| Primer Coating | — | Yes |
| Soft Touch Coating | — | Yes |
| Spray Painting | — | Yes |
| Tinted Coating | — | Yes |
| UV Coating | — | Yes |
| Vacuum Metallization | — | Yes |
| Waterproof Coating | — | Yes |
Dental Surgical Guide Resin vs Rigid 10K — frequently asked
Is Rigid 10K stronger than Dental Surgical Guide Resin?
Yes. Rigid 10K has a typical tensile strength of 75 MPa (10.9 ksi) against 55 MPa (7.98 ksi) for Dental Surgical Guide Resin — about 36% more.
Which is cheaper, Dental Surgical Guide Resin or Rigid 10K?
Rigid 10K is the lower-cost material: it sits in the premium tier ($$$) while Dental Surgical Guide Resin is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Dental Surgical Guide Resin or Rigid 10K?
Dental Surgical Guide Resin. Its machinability rates good (55/100) against fair (40/100) for Rigid 10K.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Dental Surgical Guide Resin and Rigid 10K side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.