Nickel 270 Cold Drawn vs Nickel 270 Stress Relieved
Nickel Alloy · Nickel 270 temper comparison
Nickel 270 Cold Drawn and Nickel 270 Stress Relieved are two conditions of the same nickel alloy grade, Nickel 270: Cold Drawn versus Stress Relieved. The chemistry is identical, so every difference below comes from the condition. Nickel 270 Cold Drawn is the stronger of the two: yield strength 420 MPa (60.9 ksi) against 380 MPa (55.1 ksi) for Nickel 270 Stress Relieved, about 11% more; tensile strength follows at 500 MPa (72.5 ksi) vs 470 MPa (68.2 ksi). In exchange, Nickel 270 Stress Relieved is the more ductile: elongation 20% versus 15% for Nickel 270 Cold Drawn, and Nickel 270 Cold Drawn is harder (130 HB vs 120 HB). Nickel 270 Cold Drawn runs hotter in service (600°C vs 315°C continuous).
Nickel 270 Cold DrawnChoose it when strength drives the design, or when the part sees heat.
Nickel 270 Stress RelievedChoose it when the part is bent, formed or impact-loaded.
Nickel 270 Cold Drawn vs Nickel 270 Stress Relieved: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Nickel 270 Cold DrawnNickel 270 Stress Relieved
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 207 GPa30 Msi · Shear Modulus 76 GPa11 Msi · Bulk Modulus 180 GPa26.1 Msi · Poisson's Ratio 0.31
Physical
Density and transition temperatures.
Same in both: Density 8.89 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,454°C2,649 °F · Liquidus Temperature 1,455°C2,651 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 456 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 13.3 µm/m·K7.4 µin/in·°F · Latent Heat of Fusion 297 J/g128 BTU/lb · Min Service Temperature -250°C-418 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 22 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Same in both: Formability (cold) 55 / 100 · Brazeability / Solderability 80 / 100 · Polishability 82 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 220 MJ/kg94,583 BTU/lb · Embodied Carbon (primary production) 14 kg CO₂/kg · Embodied Water 150 L/kg18 gal/lb · Typical Recycled Content 2%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Nickel 270 Cold Drawn vs Nickel 270 Stress Relieved — frequently asked
Is Nickel 270 Cold Drawn stronger than Nickel 270 Stress Relieved?
Yes. Nickel 270 Cold Drawn has a typical yield strength of 420 MPa (60.9 ksi) against 380 MPa (55.1 ksi) for Nickel 270 Stress Relieved — about 11% more. Tensile strength is 500 MPa (72.5 ksi) vs 470 MPa (68.2 ksi).
Which condition does FabDigit quote by default, Cold Drawn or Stress Relieved?
Annealed is the default Nickel 270 condition in the FabDigit quote flow (neither Cold Drawn nor Stress Relieved). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Nickel 270 Cold Drawn or Nickel 270 Stress Relieved?
Nickel 270 Cold Drawn. Its weldability rates excellent (85/100) against very good (80/100) for Nickel 270 Stress Relieved.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Nickel 270 Cold Drawn and Nickel 270 Stress Relieved side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.