Nickel 201-ANN vs Nickel 201-H24
Nickel Alloy · Nickel 201 temper comparison
Nickel 201-ANN and Nickel 201-H24 are two conditions of the same nickel alloy grade, Nickel 201: ANN (annealed) versus H24 (strain hardened and partially annealed, half hard). The chemistry is identical, so every difference below comes from the condition. Nickel 201-H24 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 105 MPa (15.2 ksi) for Nickel 201-ANN, about 3.6 times as much; tensile strength follows at 510 MPa (74 ksi) vs 415 MPa (60.2 ksi). In exchange, Nickel 201-ANN is the more ductile: elongation 47% versus 15% for Nickel 201-H24, and Nickel 201-H24 is harder (160 HB vs 90 HB). Nickel 201-ANN runs hotter in service (650°C vs 315°C continuous). On the shop floor, Nickel 201-H24 machines more easily (fair vs poor).
Nickel 201-ANNChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Nickel 201-H24Choose it when strength drives the design, or when the part is machined in volume.
Nickel 201-ANN vs Nickel 201-H24: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 78 GPa11.3 Msi · Bulk Modulus 180 GPa26.1 Msi · Poisson's Ratio 0.31 · Charpy V-Notch Impact (RT) 250 J184 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 8.89 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,435°C2,615 °F · Liquidus Temperature 1,446°C2,635 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 79 W/m·K45.6 BTU/hr·ft·°F · Specific Heat Capacity 456 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 13.3 µm/m·K7.4 µin/in·°F · Latent Heat of Fusion 297 J/g128 BTU/lb · Min Service Temperature -250°C-418 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 20 % IACS · Electrical Resistivity 8.5×10⁻⁸ Ω·m3.35 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 75 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 165 MJ/kg70,937 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 400 L/kg47.9 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Nickel 201-ANN vs Nickel 201-H24 — frequently asked
Is Nickel 201-H24 stronger than Nickel 201-ANN?
Yes. Nickel 201-H24 has a typical yield strength of 380 MPa (55.1 ksi) against 105 MPa (15.2 ksi) for Nickel 201-ANN — about 3.6 times as much. Tensile strength is 510 MPa (74 ksi) vs 415 MPa (60.2 ksi).
Which condition does FabDigit quote by default, ANN or H24?
ANN is the default Nickel 201 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, Nickel 201-ANN or Nickel 201-H24?
Nickel 201-H24. Its machinability rates fair (45/100) against poor (30/100) for Nickel 201-ANN; for welding the order is Nickel 201-ANN first (excellent, 85/100) then Nickel 201-H24 (very good, 78/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Nickel 201-ANN and Nickel 201-H24 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.