Nickel Alloy Incoloy 800HT-CD vs Incoloy 800HT CD-ANN
Nickel Alloy · Incoloy 800HT temper comparison
Incoloy 800HT-CD and Incoloy 800HT CD-ANN are two conditions of the same nickel alloy grade, Incoloy 800HT: CD (cold drawn) versus CD-ANN (cold-worked and annealed). The chemistry is identical, so every difference below comes from the condition. Incoloy 800HT-CD is the stronger of the two: yield strength 500 MPa (72.5 ksi) against 250 MPa (36.3 ksi) for Incoloy 800HT CD-ANN, about 100% more; tensile strength follows at 680 MPa (98.6 ksi) vs 540 MPa (78.3 ksi). In exchange, Incoloy 800HT CD-ANN is the more ductile: elongation 43% versus 25% for Incoloy 800HT-CD, and Incoloy 800HT-CD is harder (210 HB vs 150 HB). Incoloy 800HT CD-ANN runs hotter in service (1,100°C vs 550°C continuous).
Incoloy 800HT-CDChoose it when strength drives the design.
Incoloy 800HT CD-ANNChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Incoloy 800HT-CD vs Incoloy 800HT CD-ANN: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Incoloy 800HT-CDIncoloy 800HT CD-ANN
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 196 GPa28.4 Msi · Shear Modulus 76 GPa11 Msi · Bulk Modulus 200 GPa29 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 7.94 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,357°C2,475 °F · Liquidus Temperature 1,385°C2,525 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 11.5 W/m·K6.6 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 14.4 µm/m·K8 µin/in·°F · Latent Heat of Fusion 290 J/g125 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.8 % IACS · Electrical Resistivity 9.9×10⁻⁷ Ω·m39 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Polishability
Same in both: Machinability 28 / 100 · Weldability 75 / 100 · Brazeability / Solderability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 110 MJ/kg47,292 BTU/lb · Embodied Carbon (primary production) 7.5 kg CO₂/kg · Embodied Water 200 L/kg24 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Incoloy 800HT-CD vs Incoloy 800HT CD-ANN — frequently asked
Is Incoloy 800HT-CD stronger than Incoloy 800HT CD-ANN?
Yes. Incoloy 800HT-CD has a typical yield strength of 500 MPa (72.5 ksi) against 250 MPa (36.3 ksi) for Incoloy 800HT CD-ANN — about 100% more. Tensile strength is 680 MPa (98.6 ksi) vs 540 MPa (78.3 ksi).
Which condition does FabDigit quote by default, CD or CD-ANN?
ANN is the default Incoloy 800HT condition in the FabDigit quote flow (neither CD nor CD-ANN). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose Incoloy 800HT-CD over Incoloy 800HT CD-ANN?
Pick Incoloy 800HT-CD when strength drives the design. Pick Incoloy 800HT CD-ANN when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Incoloy 800HT-CD and Incoloy 800HT CD-ANN side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.