Nickel Alloy Hastelloy G-2-CD vs Hastelloy G-2 CW-H
Nickel Alloy · Hastelloy G-2 temper comparison
Hastelloy G-2-CD and Hastelloy G-2 CW-H are two conditions of the same nickel alloy grade, Hastelloy G-2: CD (cold drawn) versus CW-H (cold Worked / Hard strip and tube). The chemistry is identical, so every difference below comes from the condition. Hastelloy G-2 CW-H is the stronger of the two: yield strength 720 MPa (104 ksi) against 550 MPa (79.8 ksi) for Hastelloy G-2-CD, about 31% more; tensile strength follows at 930 MPa (135 ksi) vs 790 MPa (115 ksi). In exchange, Hastelloy G-2-CD is the more ductile: elongation 28% versus 12% for Hastelloy G-2 CW-H, and Hastelloy G-2 CW-H is harder (285 HB vs 240 HB). On the shop floor, Hastelloy G-2-CD welds better (68 vs 55 out of 100).
Hastelloy G-2-CDChoose it when the part is bent, formed or impact-loaded, or when it will be welded.
Hastelloy G-2 CW-HChoose it when strength drives the design.
Hastelloy G-2-CD vs Hastelloy G-2 CW-H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Hastelloy G-2-CDHastelloy G-2 CW-H
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Shear Modulus 77 GPa11.2 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 8.14 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,330°C2,426 °F · Liquidus Temperature 1,390°C2,534 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 440 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 13.6 µm/m·K7.6 µin/in·°F · Latent Heat of Fusion 290 J/g125 BTU/lb · Max Service Temperature (continuous) 480°C896 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.15 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 55 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 150 MJ/kg64,488 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 350 L/kg41.9 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Hastelloy G-2-CD vs Hastelloy G-2 CW-H — frequently asked
Is Hastelloy G-2 CW-H stronger than Hastelloy G-2-CD?
Yes. Hastelloy G-2 CW-H has a typical yield strength of 720 MPa (104 ksi) against 550 MPa (79.8 ksi) for Hastelloy G-2-CD — about 31% more. Tensile strength is 930 MPa (135 ksi) vs 790 MPa (115 ksi).
Which condition does FabDigit quote by default, CD or CW-H?
SA is the default Hastelloy G-2 condition in the FabDigit quote flow (neither CD nor CW-H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, Hastelloy G-2-CD or Hastelloy G-2 CW-H?
Hastelloy G-2-CD, by a small margin. Both rate poor for machinability — 25/100 against 16/100 for Hastelloy G-2 CW-H; for welding the order is Hastelloy G-2-CD first (good, 68/100) then Hastelloy G-2 CW-H (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Hastelloy G-2-CD and Hastelloy G-2 CW-H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.