Nickel Alloy Hastelloy C-22-CD vs Hastelloy C-22 HR-A
Nickel Alloy · Hastelloy C-22 temper comparison
Hastelloy C-22-CD and Hastelloy C-22 HR-A are two conditions of the same nickel alloy grade, Hastelloy C-22: CD (cold drawn) versus HR-A (hot rolled, solution annealed and pickled plate). The chemistry is identical, so every difference below comes from the condition. Hastelloy C-22-CD is the stronger of the two: yield strength 650 MPa (94.3 ksi) against 380 MPa (55.1 ksi) for Hastelloy C-22 HR-A, about 71% more; tensile strength follows at 950 MPa (138 ksi) vs 780 MPa (113 ksi). In exchange, Hastelloy C-22 HR-A is the more ductile: elongation 58% versus 32% for Hastelloy C-22-CD, and Hastelloy C-22-CD is harder (250 HB vs 187 HB). Hastelloy C-22 HR-A runs hotter in service (1,000°C vs 480°C continuous).
Hastelloy C-22-CDChoose it when strength drives the design.
Hastelloy C-22 HR-AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Hastelloy C-22-CD vs Hastelloy C-22 HR-A: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Hastelloy C-22-CDHastelloy C-22 HR-A
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 206 GPa29.9 Msi · Shear Modulus 79 GPa11.5 Msi · Bulk Modulus 180 GPa26.1 Msi · Poisson's Ratio 0.31
Physical
Density and transition temperatures.
Same in both: Density 8.69 g/cm³0.31 lb/in³ · Melting Point (Solidus) 1,357°C2,475 °F · Liquidus Temperature 1,399°C2,550 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 10.1 W/m·K5.8 BTU/hr·ft·°F · Specific Heat Capacity 414 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.4 µm/m·K6.9 µin/in·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 1.5 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 50 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 145 MJ/kg62,339 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Hastelloy C-22-CD vs Hastelloy C-22 HR-A — frequently asked
Is Hastelloy C-22-CD stronger than Hastelloy C-22 HR-A?
Yes. Hastelloy C-22-CD has a typical yield strength of 650 MPa (94.3 ksi) against 380 MPa (55.1 ksi) for Hastelloy C-22 HR-A — about 71% more. Tensile strength is 950 MPa (138 ksi) vs 780 MPa (113 ksi).
Which condition does FabDigit quote by default, CD or HR-A?
SA is the default Hastelloy C-22 condition in the FabDigit quote flow (neither CD nor HR-A). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Hastelloy C-22-CD or Hastelloy C-22 HR-A?
Hastelloy C-22 HR-A. Its weldability rates excellent (85/100) against very good (78/100) for Hastelloy C-22-CD.