Particleboard vs Plywood
Natural Material · grade comparison
Particleboard and Plywood are both natural material grades. Plywood is the stronger of the two: tensile strength 30 MPa (4.35 ksi) against 9 MPa (1.31 ksi) for Particleboard, about 3.3 times as much. Plywood is the more ductile: elongation 1% versus 0.6% for Particleboard. Plywood is lighter (0.55 g/cm³ vs 0.68 g/cm³ for Particleboard) and Plywood is stiffer (9 GPa vs 2.4 GPa). On the shop floor, Plywood machines more easily (excellent vs good).
PlywoodChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Particleboard vs Plywood: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all natural material grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all natural material grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Mohs
Physical
Density and transition temperatures.
Density
Porosity
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every natural material grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Particleboard | Plywood |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Particleboard vs Plywood — frequently asked
Is Plywood stronger than Particleboard?
Yes. Plywood has a typical tensile strength of 30 MPa (4.35 ksi) against 9 MPa (1.31 ksi) for Particleboard — about 3.3 times as much.
Which is cheaper, Particleboard or Plywood?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Particleboard or Plywood?
Plywood. Its machinability rates excellent (88/100) against good (65/100) for Particleboard.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Particleboard and Plywood side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.