Magnesium Alloy ZC63A-F vs ZC63A-T4
Magnesium Alloy · ZC63A temper comparison
ZC63A-F and ZC63A-T4 are two conditions of the same magnesium alloy grade, ZC63A: F (as fabricated) versus T4 (solution heat treated and naturally aged). The chemistry is identical, so every difference below comes from the condition. ZC63A-F is the stronger of the two: yield strength 110 MPa (16 ksi) against 100 MPa (14.5 ksi) for ZC63A-T4, about 10% more. In exchange, ZC63A-T4 is the more ductile: elongation 8% versus 3% for ZC63A-F. ZC63A-T4 runs hotter in service (150°C vs 130°C continuous) and ZC63A-F conducts electricity better (24 % IACS vs 21 % IACS).
ZC63A-FChoose it when strength drives the design.
ZC63A-T4Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
ZC63A-F vs ZC63A-T4: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 45 GPa6.5 Msi · Shear Modulus 17 GPa2.5 Msi · Bulk Modulus 45 GPa6.5 Msi · Poisson's Ratio 0.35 · Fatigue Strength (Endurance Limit) 70 MPa10.2 ksi
Physical
Density and transition temperatures.
Same in both: Density 1.87 g/cm³0.07 lb/in³ · Melting Point (Solidus) 465°C869 °F · Liquidus Temperature 635°C1,175 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 1,000 J/kg·K0.24 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 27 µm/m·K15 µin/in·°F · Latent Heat of Fusion 340 J/g146 BTU/lb · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -1.55 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 45 / 100 · Castability 80 / 100 · Brazeability / Solderability 20 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 330 MJ/kg141,875 BTU/lb · Embodied Carbon (primary production) 33 kg CO₂/kg · Embodied Water 500 L/kg59.9 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every magnesium alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
ZC63A-F vs ZC63A-T4 — frequently asked
Is ZC63A-F stronger than ZC63A-T4?
Yes. ZC63A-F has a typical yield strength of 110 MPa (16 ksi) against 100 MPa (14.5 ksi) for ZC63A-T4 — about 10% more. Tensile strength is 175 MPa (25.4 ksi) vs 200 MPa (29 ksi).
Which condition does FabDigit quote by default, F or T4?
T6 is the default ZC63A condition in the FabDigit quote flow (neither F nor T4). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose ZC63A-F over ZC63A-T4?
Pick ZC63A-F when strength drives the design. Pick ZC63A-T4 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in ZC63A-F and ZC63A-T4 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.