Magnesium Alloy EV31A vs ZM10
Magnesium Alloy · grade comparison
Magnesium Alloy EV31A and ZM10 are both magnesium alloy grades. ZM10 is the stronger of the two: yield strength 140 MPa (20.3 ksi) against 110 MPa (16 ksi) for EV31A, about 27% more; tensile strength follows at 260 MPa (37.7 ksi) vs 195 MPa (28.3 ksi). In exchange, EV31A is the more ductile: elongation 4% versus 2.5% for ZM10, and ZM10 is harder (80 HB vs 55 HB). EV31A runs hotter in service (150°C vs 130°C continuous) and EV31A conducts heat better (100 W/m·K vs 72 W/m·K). On the shop floor, EV31A welds better (very good vs good) and EV31A sits in a lower cost tier (standard, $$) than ZM10 (premium, $$$).
EV31AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
ZM10Choose it when strength drives the design.
EV31A vs ZM10: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all magnesium alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 17 GPa2.5 Msi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 1,000 J/kg·K0.24 BTU/lb·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Same in both: Formability (cold) 10 / 100 · Brazeability / Solderability 20 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every magnesium alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | EV31A | ZM10 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | As Cast | — |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Chem Film (Alodine) | Yes | — |
| E-Coating | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
EV31A vs ZM10 — frequently asked
Is ZM10 stronger than EV31A?
Yes. ZM10 has a typical yield strength of 140 MPa (20.3 ksi) against 110 MPa (16 ksi) for EV31A — about 27% more. Tensile strength is 260 MPa (37.7 ksi) vs 195 MPa (28.3 ksi).
Which is cheaper, EV31A or ZM10?
EV31A is the lower-cost material: it sits in the standard tier ($$) while ZM10 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, EV31A or ZM10?
ZM10, by a small margin. Both rate excellent for machinability — 95/100 against 90/100 for EV31A; for welding the order is EV31A first (very good, 72/100) then ZM10 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in EV31A and ZM10 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.