Copper Alloy TU1-H02 vs TU1-H80
Copper Alloy · TU1 temper comparison
TU1-H02 and TU1-H80 are two conditions of the same copper alloy grade, TU1: H02 (half hard) versus H80 (hard drawn). The chemistry is identical, so every difference below comes from the condition. TU1-H80 is the stronger of the two: yield strength 345 MPa (50 ksi) against 250 MPa (36.3 ksi) for TU1-H02, about 38% more; tensile strength follows at 379 MPa (55 ksi) vs 290 MPa (42.1 ksi). In exchange, TU1-H02 is the more ductile: elongation 14% versus 10% for TU1-H80, and TU1-H80 is harder (100 HB vs 75 HB). TU1-H80 is stiffer (128 GPa vs 120 GPa).
TU1-H02Choose it when the part is bent, formed or impact-loaded.
TU1-H80Choose it when strength drives the design.
TU1-H02 vs TU1-H80: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,083°C1,981 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17 µm/m·K9.4 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Weldability 70 / 100 · Castability 40 / 100 · Brazeability / Solderability 95 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 60 MJ/kg25,795 BTU/lb · Embodied Carbon (primary production) 4 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 15%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
TU1-H02 vs TU1-H80 — frequently asked
Is TU1-H80 stronger than TU1-H02?
Yes. TU1-H80 has a typical yield strength of 345 MPa (50 ksi) against 250 MPa (36.3 ksi) for TU1-H02 — about 38% more. Tensile strength is 379 MPa (55 ksi) vs 290 MPa (42.1 ksi).
Which condition does FabDigit quote by default, H02 or H80?
OS050 is the default TU1 condition in the FabDigit quote flow (neither H02 nor H80). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, TU1-H02 or TU1-H80?
TU1-H80, by a small margin. Both rate fair for machinability — 40/100 against 35/100 for TU1-H02.
Ready to make it?
Upload a CAD file and FabDigit prices the part in TU1-H02 and TU1-H80 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.