Copper Alloy CC495K-GS vs CC495K-GZ
Copper Alloy · CC495K temper comparison
CC495K-GS and CC495K-GZ are two conditions of the same copper alloy grade, CC495K: GS (sand cast) versus GZ (centrifugally cast). The chemistry is identical, so every difference below comes from the condition. CC495K-GZ is the stronger of the two: yield strength 130 MPa (18.9 ksi) against 100 MPa (14.5 ksi) for CC495K-GS, about 30% more; tensile strength follows at 260 MPa (37.7 ksi) vs 220 MPa (31.9 ksi). In exchange, CC495K-GS is the more ductile: elongation 12% versus 10% for CC495K-GZ, and CC495K-GZ is harder (72 HB vs 65 HB). CC495K-GZ is stiffer (76 GPa vs 72 GPa).
CC495K-GSChoose it when the part is bent, formed or impact-loaded.
CC495K-GZChoose it when strength drives the design.
CC495K-GS vs CC495K-GZ: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 28 GPa4.1 Msi · Bulk Modulus 78 GPa11.3 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.9 g/cm³0.32 lb/in³ · Melting Point (Solidus) 762°C1,404 °F · Liquidus Temperature 930°C1,706 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 47 W/m·K27.2 BTU/hr·ft·°F · Specific Heat Capacity 251 J/kg·K0.06 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.5 µm/m·K10.3 µin/in·°F · Latent Heat of Fusion 170 J/g73.1 BTU/lb · Max Service Temperature (continuous) 250°C482 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10 % IACS · Electrical Resistivity 1.72×10⁻⁷ Ω·m6.77 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Same in both: Machinability 85 / 100 · Machinability Rating (AISI 1212 = 100 %) 80% · Weldability 10 / 100 · Formability (cold) 10 / 100 · Castability 88 / 100 · Brazeability / Solderability 60 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
CC495K-GS vs CC495K-GZ — frequently asked
Is CC495K-GZ stronger than CC495K-GS?
Yes. CC495K-GZ has a typical yield strength of 130 MPa (18.9 ksi) against 100 MPa (14.5 ksi) for CC495K-GS — about 30% more. Tensile strength is 260 MPa (37.7 ksi) vs 220 MPa (31.9 ksi).
Which condition does FabDigit quote by default, GS or GZ?
GC is the default CC495K condition in the FabDigit quote flow (neither GS nor GZ). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose CC495K-GS over CC495K-GZ?
Pick CC495K-GS when the part is bent, formed or impact-loaded. Pick CC495K-GZ when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in CC495K-GS and CC495K-GZ side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.