Copper Alloy CC491K-GM vs CC491K-GZ
Copper Alloy · CC491K temper comparison
CC491K-GM and CC491K-GZ are two conditions of the same copper alloy grade, CC491K: GM (permanent mould (chill/gravity die) cast) versus GZ (centrifugally cast). The chemistry is identical, so every difference below comes from the condition. CC491K-GZ is the stronger of the two: yield strength 130 MPa (18.9 ksi) against 120 MPa (17.4 ksi) for CC491K-GM, about 8% more; tensile strength follows at 270 MPa (39.2 ksi) vs 250 MPa (36.3 ksi). CC491K-GZ is the more ductile: elongation 14% versus 12% for CC491K-GM.
CC491K-GZChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
CC491K-GM vs CC491K-GZ: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Same in both: Shear Modulus 37 GPa5.4 Msi · Bulk Modulus 104 GPa15.1 Msi · Poisson's Ratio 0.34 · Hardness, Brinell 65 HB · Hardness, Rockwell B 35 HRB · Hardness, Vickers 68 HV
Physical
Density and transition temperatures.
Same in both: Density 8.83 g/cm³0.32 lb/in³ · Melting Point (Solidus) 854°C1,569 °F · Liquidus Temperature 1,010°C1,850 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 72 W/m·K41.6 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18 µm/m·K10 µin/in·°F · Latent Heat of Fusion 170 J/g73.1 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 15 % IACS · Electrical Resistivity 1.15×10⁻⁷ Ω·m4.53 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Same in both: Machinability 85 / 100 · Machinability Rating (AISI 1212 = 100 %) 84% · Weldability 25 / 100 · Formability (cold) 15 / 100 · Castability 90 / 100 · Brazeability / Solderability 75 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 52 MJ/kg22,356 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 80%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
CC491K-GM vs CC491K-GZ — frequently asked
Is CC491K-GZ stronger than CC491K-GM?
Yes. CC491K-GZ has a typical yield strength of 130 MPa (18.9 ksi) against 120 MPa (17.4 ksi) for CC491K-GM — about 8% more. Tensile strength is 270 MPa (39.2 ksi) vs 250 MPa (36.3 ksi).
Which condition does FabDigit quote by default, GM or GZ?
GS is the default CC491K condition in the FabDigit quote flow (neither GM nor GZ). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose CC491K-GM over CC491K-GZ?
Pick CC491K-GZ when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in CC491K-GM and CC491K-GZ side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.