Copper Alloy C96200-M01 vs C96200-M02
Copper Alloy · C96200 temper comparison
C96200-M01 and C96200-M02 are two conditions of the same copper alloy grade, C96200: M01 (as sand cast) versus M02 (as centrifugally cast). The chemistry is identical, so every difference below comes from the condition. C96200-M02 is the stronger of the two: yield strength 195 MPa (28.3 ksi) against 179 MPa (26 ksi) for C96200-M01, about 9% more; tensile strength follows at 345 MPa (50 ksi) vs 317 MPa (46 ksi). C96200-M02 is the more ductile: elongation 28% versus 25% for C96200-M01, and C96200-M02 is harder (85 HB vs 80 HB).
C96200-M02Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
C96200-M01 vs C96200-M02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 124 GPa18 Msi · Shear Modulus 47 GPa6.8 Msi · Bulk Modulus 120 GPa17.4 Msi · Poisson's Ratio 0.32
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,099°C2,010 °F · Liquidus Temperature 1,149°C2,100 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 45 W/m·K26 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Latent Heat of Fusion 200 J/g86 BTU/lb · Max Service Temperature (continuous) 315°C599 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 9.5 % IACS · Electrical Resistivity 1.9×10⁻⁷ Ω·m7.48 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.26 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Same in both: Machinability 30 / 100 · Machinability Rating (AISI 1212 = 100 %) 20% · Weldability 75 / 100 · Castability 60 / 100 · Brazeability / Solderability 70 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 72 MJ/kg30,954 BTU/lb · Embodied Carbon (primary production) 5.2 kg CO₂/kg · Embodied Water 400 L/kg47.9 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C96200-M01 vs C96200-M02 — frequently asked
Is C96200-M02 stronger than C96200-M01?
Yes. C96200-M02 has a typical yield strength of 195 MPa (28.3 ksi) against 179 MPa (26 ksi) for C96200-M01 — about 9% more. Tensile strength is 345 MPa (50 ksi) vs 317 MPa (46 ksi).
Which condition does FabDigit quote by default, M01 or M02?
M01 is the default C96200 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C96200-M01 over C96200-M02?
Pick C96200-M02 when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C96200-M01 and C96200-M02 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.