Copper Alloy C92800-M01 vs C92800-M07
Copper Alloy · C92800 temper comparison
C92800-M01 and C92800-M07 are two conditions of the same copper alloy grade, C92800: M01 (as sand cast) versus M07 (as continuous cast). The chemistry is identical, so every difference below comes from the condition. C92800-M07 is the stronger of the two: yield strength 205 MPa (29.7 ksi) against 179 MPa (26 ksi) for C92800-M01, about 15% more; tensile strength follows at 310 MPa (45 ksi) vs 276 MPa (40 ksi). C92800-M07 is harder — 95 HB against 85 HB for C92800-M01 — which matters for wear surfaces and threads.
C92800-M07Choose it when strength drives the design, or when surface hardness matters.
C92800-M01 vs C92800-M07: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Shear Modulus 39 GPa5.7 Msi · Bulk Modulus 103 GPa14.9 Msi · Poisson's Ratio 0.34 · Elongation at Break 1% · Reduction in Area 1%
Physical
Density and transition temperatures.
Same in both: Density 8.8 g/cm³0.32 lb/in³ · Melting Point (Solidus) 830°C1,526 °F · Liquidus Temperature 1,000°C1,832 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 47 W/m·K27.2 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18 µm/m·K10 µin/in·°F · Latent Heat of Fusion 170 J/g73.1 BTU/lb · Max Service Temperature (continuous) 230°C446 °F · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 11 % IACS · Electrical Resistivity 1.57×10⁻⁷ Ω·m6.18 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.31 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 10 / 100 · Formability (cold) 5 / 100 · Castability 75 / 100 · Brazeability / Solderability 70 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 62 MJ/kg26,655 BTU/lb · Embodied Carbon (primary production) 4.5 kg CO₂/kg · Embodied Water 320 L/kg38.3 gal/lb · Typical Recycled Content 50%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C92800-M01 vs C92800-M07 — frequently asked
Is C92800-M07 stronger than C92800-M01?
Yes. C92800-M07 has a typical yield strength of 205 MPa (29.7 ksi) against 179 MPa (26 ksi) for C92800-M01 — about 15% more. Tensile strength is 310 MPa (45 ksi) vs 276 MPa (40 ksi).
Which condition does FabDigit quote by default, M01 or M07?
M01 is the default C92800 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C92800-M01 or C92800-M07?
C92800-M07, by a small margin. Both rate very good for machinability — 75/100 against 70/100 for C92800-M01.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C92800-M01 and C92800-M07 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.