Copper Alloy C84100-M02 vs C84100-M07
Copper Alloy · C84100 temper comparison
C84100-M02 and C84100-M07 are two conditions of the same copper alloy grade, C84100: M02 (as centrifugally cast) versus M07 (as continuous cast). The chemistry is identical, so every difference below comes from the condition. C84100-M07 is the stronger of the two: yield strength 110 MPa (16 ksi) against 100 MPa (14.5 ksi) for C84100-M02, about 10% more. In exchange, C84100-M02 is the more ductile: elongation 28% versus 25% for C84100-M07, and C84100-M07 is harder (58 HB vs 55 HB).
C84100-M02Choose it when the part is bent, formed or impact-loaded.
C84100-M07Choose it when strength drives the design.
C84100-M02 vs C84100-M07: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 90 GPa13.1 Msi · Shear Modulus 34 GPa4.9 Msi · Bulk Modulus 105 GPa15.2 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.6 g/cm³0.31 lb/in³ · Melting Point (Solidus) 855°C1,571 °F · Liquidus Temperature 1,000°C1,832 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 72 W/m·K41.6 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.7 µm/m·K11.5 µin/in·°F · Latent Heat of Fusion 175 J/g75.2 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 16.5 % IACS · Electrical Resistivity 1.05×10⁻⁷ Ω·m4.13 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 58 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 25 / 100 · Formability (cold) 15 / 100 · Castability 85 / 100 · Brazeability / Solderability 80 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 45 MJ/kg19,347 BTU/lb · Embodied Carbon (primary production) 3 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 85%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C84100-M02 vs C84100-M07 — frequently asked
Is C84100-M07 stronger than C84100-M02?
Yes. C84100-M07 has a typical yield strength of 110 MPa (16 ksi) against 100 MPa (14.5 ksi) for C84100-M02 — about 10% more. Tensile strength is 234 MPa (33.9 ksi) vs 228 MPa (33.1 ksi).
Which condition does FabDigit quote by default, M02 or M07?
M01 is the default C84100 condition in the FabDigit quote flow (neither M02 nor M07). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C84100-M02 or C84100-M07?
C84100-M07. Its machinability rates excellent (85/100) against very good (80/100) for C84100-M02.