Copper Alloy C82800-TB00 vs C82800-TF00
Copper Alloy · C82800 temper comparison
C82800-TB00 and C82800-TF00 are two conditions of the same copper alloy grade, C82800: TB00 (solution heat treated) versus TF00 (solution heat treated and precipitation hardened). The chemistry is identical, so every difference below comes from the condition. C82800-TF00 is the stronger of the two: yield strength 1,000 MPa (145 ksi) against 240 MPa (34.8 ksi) for C82800-TB00, about 4.2 times as much; tensile strength follows at 1,069 MPa (155 ksi) vs 520 MPa (75.4 ksi). In exchange, C82800-TB00 is the more ductile: elongation 12% versus 0.5% for C82800-TF00, and C82800-TF00 is harder (400 HB vs 155 HB). C82800-TF00 runs hotter in service (200°C vs 150°C continuous) and C82800-TF00 conducts heat better (105 W/m·K vs 62 W/m·K).
C82800-TB00Choose it when the part is bent, formed or impact-loaded.
C82800-TF00Choose it when strength drives the design, or when the part sees heat.
C82800-TB00 vs C82800-TF00: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 131 GPa19 Msi · Shear Modulus 50 GPa7.3 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.3 · Compressive Strength 1,300 MPa189 ksi · Shear Strength 690 MPa100 ksi · Fatigue Strength (Endurance Limit) 240 MPa34.8 ksi · Fracture Toughness (K_IC) 20 MPa·√m18.2 ksi·√in · Hardness, Rockwell C 43 HRC · Hardness, Vickers 420 HV
Physical
Density and transition temperatures.
Same in both: Density 8.25 g/cm³0.3 lb/in³ · Melting Point (Solidus) 857°C1,575 °F · Liquidus Temperature 954°C1,749 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 419 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.22 V · Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Weldability 40 / 100 · Castability 80 / 100 · Brazeability / Solderability 55 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 130 MJ/kg55,890 BTU/lb · Embodied Carbon (primary production) 8.5 kg CO₂/kg · Embodied Water 350 L/kg41.9 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C82800-TB00 vs C82800-TF00 — frequently asked
Is C82800-TF00 stronger than C82800-TB00?
Yes. C82800-TF00 has a typical yield strength of 1,000 MPa (145 ksi) against 240 MPa (34.8 ksi) for C82800-TB00 — about 4.2 times as much. Tensile strength is 1,069 MPa (155 ksi) vs 520 MPa (75.4 ksi).
Which condition does FabDigit quote by default, TB00 or TF00?
TF00 is the default C82800 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C82800-TB00 or C82800-TF00?
C82800-TF00. Its machinability rates fair (35/100) against poor (28/100) for C82800-TB00.