Copper Alloy C82200-M vs C82200-TB00
Copper Alloy · C82200 temper comparison
C82200-M and C82200-TB00 are two conditions of the same copper alloy grade, C82200: M (thermomechanically controlled processed) versus TB00 (solution heat treated). The chemistry is identical, so every difference below comes from the condition. C82200-M is the stronger of the two: yield strength 160 MPa (23.2 ksi) against 125 MPa (18.1 ksi) for C82200-TB00, about 28% more; tensile strength follows at 345 MPa (50 ksi) vs 275 MPa (39.9 ksi). In exchange, C82200-TB00 is the more ductile: elongation 30% versus 20% for C82200-M, and C82200-M is harder (80 HB vs 55 HB). C82200-M runs hotter in service (180°C vs 150°C continuous) and C82200-M conducts electricity better (25 % IACS vs 20 % IACS). On the shop floor, C82200-M machines more easily (45 vs 35 out of 100).
C82200-MChoose it when strength drives the design, or when the part sees heat.
C82200-TB00Choose it when the part is bent, formed or impact-loaded.
C82200-M vs C82200-TB00: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 130 GPa18.9 Msi · Shear Modulus 50 GPa7.3 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.3 · Hardness, Vickers 205 HV
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 8.75 g/cm³0.32 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 420 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.8 µm/m·K9.9 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Brazeability / Solderability
Polishability
Same in both: Formability (cold) 15 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C82200-M vs C82200-TB00 — frequently asked
Is C82200-M stronger than C82200-TB00?
Yes. C82200-M has a typical yield strength of 160 MPa (23.2 ksi) against 125 MPa (18.1 ksi) for C82200-TB00 — about 28% more. Tensile strength is 345 MPa (50 ksi) vs 275 MPa (39.9 ksi).
Which condition does FabDigit quote by default, M or TB00?
TF00 is the default C82200 condition in the FabDigit quote flow (neither M nor TB00). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C82200-M or C82200-TB00?
C82200-M, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for C82200-TB00; for welding the order is C82200-M first (good, 55/100) then C82200-TB00 (fair, 50/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C82200-M and C82200-TB00 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.