Copper Alloy C71000-H02 vs C71000-O61
Copper Alloy · C71000 temper comparison
C71000-H02 and C71000-O61 are two conditions of the same copper alloy grade, C71000: H02 (half hard) versus O61 (annealed). The chemistry is identical, so every difference below comes from the condition. C71000-H02 is the stronger of the two: yield strength 415 MPa (60.2 ksi) against 110 MPa (16 ksi) for C71000-O61, about 3.8 times as much; tensile strength follows at 480 MPa (69.6 ksi) vs 340 MPa (49.3 ksi). In exchange, C71000-O61 is the more ductile: elongation 40% versus 12% for C71000-H02, and C71000-H02 is harder (135 HB vs 75 HB). C71000-O61 runs hotter in service (320°C vs 200°C continuous).
C71000-H02Choose it when strength drives the design.
C71000-O61Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C71000-H02 vs C71000-O61: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 138 GPa20 Msi · Shear Modulus 52 GPa7.5 Msi · Bulk Modulus 132 GPa19.1 Msi · Poisson's Ratio 0.32 · Reduction in Area 65% · Hardness, Vickers 80 HV
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,099°C2,010 °F · Liquidus Temperature 1,149°C2,100 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 37 W/m·K21.4 BTU/hr·ft·°F · Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 15.6 µm/m·K8.7 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 6.5 % IACS · Electrical Resistivity 2.65×10⁻⁷ Ω·m10.4 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.27 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Castability 45 / 100 · Brazeability / Solderability 88 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 72 MJ/kg30,954 BTU/lb · Embodied Carbon (primary production) 5.2 kg CO₂/kg · Embodied Water 320 L/kg38.3 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C71000-H02 vs C71000-O61 — frequently asked
Is C71000-H02 stronger than C71000-O61?
Yes. C71000-H02 has a typical yield strength of 415 MPa (60.2 ksi) against 110 MPa (16 ksi) for C71000-O61 — about 3.8 times as much. Tensile strength is 480 MPa (69.6 ksi) vs 340 MPa (49.3 ksi).
Which condition does FabDigit quote by default, H02 or O61?
O61 is the default C71000 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C71000-H02 or C71000-O61?
C71000-H02, by a small margin. Both rate poor for machinability — 25/100 against 20/100 for C71000-O61; for welding the order is C71000-O61 first (excellent, 85/100) then C71000-H02 (very good, 80/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C71000-H02 and C71000-O61 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.