Copper Alloy C70700-H01 vs C70700-M20
Copper Alloy · C70700 temper comparison
C70700-H01 and C70700-M20 are two conditions of the same copper alloy grade, C70700: H01 (quarter hard) versus M20 (as hot rolled). The chemistry is identical, so every difference below comes from the condition. C70700-H01 is the stronger of the two: yield strength 240 MPa (34.8 ksi) against 125 MPa (18.1 ksi) for C70700-M20, about 92% more; tensile strength follows at 345 MPa (50 ksi) vs 305 MPa (44.2 ksi). In exchange, C70700-M20 is the more ductile: elongation 35% versus 30% for C70700-H01, and C70700-H01 is harder (100 HB vs 70 HB). C70700-M20 runs hotter in service (350°C vs 250°C continuous).
C70700-H01Choose it when strength drives the design.
C70700-M20Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C70700-H01 vs C70700-M20: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 124 GPa18 Msi · Shear Modulus 46 GPa6.7 Msi · Bulk Modulus 112 GPa16.2 Msi · Poisson's Ratio 0.31
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,100°C2,012 °F · Liquidus Temperature 1,145°C2,093 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 40 W/m·K23.1 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.1 µm/m·K9.5 µin/in·°F · Latent Heat of Fusion 210 J/g90.3 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V · Corrosion Resistance 78 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Castability 45 / 100 · Brazeability / Solderability 88 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 70 MJ/kg30,095 BTU/lb · Embodied Carbon (primary production) 4.8 kg CO₂/kg · Embodied Water 260 L/kg31.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C70700-H01 vs C70700-M20 — frequently asked
Is C70700-H01 stronger than C70700-M20?
Yes. C70700-H01 has a typical yield strength of 240 MPa (34.8 ksi) against 125 MPa (18.1 ksi) for C70700-M20 — about 92% more. Tensile strength is 345 MPa (50 ksi) vs 305 MPa (44.2 ksi).
Which condition does FabDigit quote by default, H01 or M20?
O61 is the default C70700 condition in the FabDigit quote flow (neither H01 nor M20). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C70700-H01 over C70700-M20?
Pick C70700-H01 when strength drives the design. Pick C70700-M20 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C70700-H01 and C70700-M20 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.