Copper Alloy C67500-H04 vs C67500-M11
Copper Alloy · C67500 temper comparison
C67500-H04 and C67500-M11 are two conditions of the same copper alloy grade, C67500: H04 (full hard) versus M11 (as forged and quenched). The chemistry is identical, so every difference below comes from the condition. C67500-H04 is the stronger of the two: yield strength 414 MPa (60 ksi) against 241 MPa (35 ksi) for C67500-M11, about 72% more; tensile strength follows at 579 MPa (84 ksi) vs 517 MPa (75 ksi). In exchange, C67500-M11 is the more ductile: elongation 26% versus 15% for C67500-H04, and C67500-H04 is harder (180 HB vs 152 HB). C67500-M11 runs hotter in service (200°C vs 180°C continuous).
C67500-H04Choose it when strength drives the design.
C67500-M11Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C67500-H04 vs C67500-M11: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Shear Modulus 39 GPa5.7 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.32 · Reduction in Area 40%
Physical
Density and transition temperatures.
Same in both: Density 8.36 g/cm³0.3 lb/in³ · Melting Point (Solidus) 865°C1,589 °F · Liquidus Temperature 888°C1,630 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 100 W/m·K57.8 BTU/hr·ft·°F · Specific Heat Capacity 376 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 21.2 µm/m·K11.8 µin/in·°F · Latent Heat of Fusion 175 J/g75.2 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 23 % IACS · Electrical Resistivity 7.2×10⁻⁸ Ω·m2.83 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.29 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 55 / 100 · Castability 65 / 100 · Brazeability / Solderability 78 / 100 · Polishability 72 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 50 MJ/kg21,496 BTU/lb · Embodied Carbon (primary production) 3.4 kg CO₂/kg · Embodied Water 320 L/kg38.3 gal/lb · Typical Recycled Content 55%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C67500-H04 vs C67500-M11 — frequently asked
Is C67500-H04 stronger than C67500-M11?
Yes. C67500-H04 has a typical yield strength of 414 MPa (60 ksi) against 241 MPa (35 ksi) for C67500-M11 — about 72% more. Tensile strength is 579 MPa (84 ksi) vs 517 MPa (75 ksi).
Which condition does FabDigit quote by default, H04 or M11?
H02 is the default C67500 condition in the FabDigit quote flow (neither H04 nor M11). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C67500-H04 over C67500-M11?
Pick C67500-H04 when strength drives the design. Pick C67500-M11 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C67500-H04 and C67500-M11 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.