Copper Alloy C67400-H01 vs C67400-O60
Copper Alloy · C67400 temper comparison
C67400-H01 and C67400-O60 are two conditions of the same copper alloy grade, C67400: H01 (quarter hard) versus O60 (soft annealed). The chemistry is identical, so every difference below comes from the condition. C67400-H01 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 260 MPa (37.7 ksi) for C67400-O60, about 46% more; tensile strength follows at 655 MPa (95 ksi) vs 585 MPa (84.8 ksi). In exchange, C67400-O60 is the more ductile: elongation 30% versus 20% for C67400-H01, and C67400-H01 is harder (175 HB vs 150 HB).
C67400-H01Choose it when strength drives the design.
C67400-O60Choose it when the part is bent, formed or impact-loaded.
C67400-H01 vs C67400-O60: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 105 GPa15.2 Msi · Shear Modulus 39 GPa5.7 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34 · Charpy V-Notch Impact (RT) 25 J18.4 ft·lbf
Physical
Density and transition temperatures.
Same in both: Density 8.36 g/cm³0.3 lb/in³ · Melting Point (Solidus) 862°C1,584 °F · Liquidus Temperature 880°C1,616 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 40 W/m·K23.1 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 21 µm/m·K11.7 µin/in·°F · Latent Heat of Fusion 170 J/g73.1 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8 % IACS · Electrical Resistivity 2.15×10⁻⁷ Ω·m8.46 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.27 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.5 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C67400-H01 vs C67400-O60 — frequently asked
Is C67400-H01 stronger than C67400-O60?
Yes. C67400-H01 has a typical yield strength of 380 MPa (55.1 ksi) against 260 MPa (37.7 ksi) for C67400-O60 — about 46% more. Tensile strength is 655 MPa (95 ksi) vs 585 MPa (84.8 ksi).
Which condition does FabDigit quote by default, H01 or O60?
M30 is the default C67400 condition in the FabDigit quote flow (neither H01 nor O60). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C67400-H01 or C67400-O60?
C67400-H01, by a small margin. Both rate poor for machinability — 30/100 against 25/100 for C67400-O60.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C67400-H01 and C67400-O60 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.