Copper Alloy C61400-H80 vs C61400-O60
Copper Alloy · C61400 temper comparison
C61400-H80 and C61400-O60 are two conditions of the same copper alloy grade, C61400: H80 (hard drawn) versus O60 (soft annealed). The chemistry is identical, so every difference below comes from the condition. C61400-H80 is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 205 MPa (29.7 ksi) for C61400-O60, about 120% more; tensile strength follows at 620 MPa (89.9 ksi) vs 505 MPa (73.2 ksi). In exchange, C61400-O60 is the more ductile: elongation 50% versus 20% for C61400-H80, and C61400-H80 is harder (185 HB vs 128 HB). On the shop floor, C61400-H80 machines more easily (34 vs 24 out of 100).
C61400-H80Choose it when strength drives the design, or when the part is machined in volume.
C61400-O60Choose it when the part is bent, formed or impact-loaded.
C61400-H80 vs C61400-O60: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.32 · Hardness, Vickers 150 HV
Physical
Density and transition temperatures.
Same in both: Density 7.89 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,040°C1,904 °F · Liquidus Temperature 1,045°C1,913 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 66.6 W/m·K38.5 BTU/hr·ft·°F · Specific Heat Capacity 376 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Latent Heat of Fusion 210 J/g90.3 BTU/lb · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 14 % IACS · Electrical Resistivity 1.23×10⁻⁷ Ω·m4.84 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V · Corrosion Resistance 76 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 50% · Castability 55 / 100 · Brazeability / Solderability 30 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C61400-H80 vs C61400-O60 — frequently asked
Is C61400-H80 stronger than C61400-O60?
Yes. C61400-H80 has a typical yield strength of 450 MPa (65.3 ksi) against 205 MPa (29.7 ksi) for C61400-O60 — about 120% more. Tensile strength is 620 MPa (89.9 ksi) vs 505 MPa (73.2 ksi).
Which condition does FabDigit quote by default, H80 or O60?
M20 is the default C61400 condition in the FabDigit quote flow (neither H80 nor O60). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C61400-H80 or C61400-O60?
C61400-H80, by a small margin. Both rate poor for machinability — 34/100 against 24/100 for C61400-O60.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C61400-H80 and C61400-O60 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.