Copper Alloy C61300-AW vs C61300-O60
Copper Alloy · C61300 temper comparison
C61300-AW and C61300-O60 are two conditions of the same copper alloy grade, C61300: AW (as-welded deposit) versus O60 (soft annealed). The chemistry is identical, so every difference below comes from the condition. C61300-AW is the stronger of the two: yield strength 260 MPa (37.7 ksi) against 205 MPa (29.7 ksi) for C61300-O60, about 27% more. In exchange, C61300-O60 is the more ductile: elongation 45% versus 30% for C61300-AW, and C61300-AW is harder (145 HB vs 128 HB).
C61300-AWChoose it when strength drives the design.
C61300-O60Choose it when the part is bent, formed or impact-loaded.
C61300-AW vs C61300-O60: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 112 GPa16.2 Msi · Poisson's Ratio 0.32 · Fatigue Strength (Endurance Limit) 195 MPa28.3 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.89 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,038°C1,900 °F · Liquidus Temperature 1,046°C1,915 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Latent Heat of Fusion 210 J/g90.3 BTU/lb · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.31 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 78 / 100 · Castability 55 / 100 · Brazeability / Solderability 32 / 100 · Polishability 72 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 260 L/kg31.2 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C61300-AW vs C61300-O60 — frequently asked
Is C61300-AW stronger than C61300-O60?
Yes. C61300-AW has a typical yield strength of 260 MPa (37.7 ksi) against 205 MPa (29.7 ksi) for C61300-O60 — about 27% more. Tensile strength is 540 MPa (78.3 ksi) vs 515 MPa (74.7 ksi).
Which condition does FabDigit quote by default, AW or O60?
M20 is the default C61300 condition in the FabDigit quote flow (neither AW nor O60). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C61300-AW over C61300-O60?
Pick C61300-AW when strength drives the design. Pick C61300-O60 when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C61300-AW and C61300-O60 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.