Copper Alloy C52100 vs C62300
Copper Alloy · grade comparison
Copper Alloy C52100 and C62300 are both copper alloy grades. C52100 is the stronger of the two: yield strength 585 MPa (84.8 ksi) against 290 MPa (42.1 ksi) for C62300, about 102% more; tensile strength follows at 660 MPa (95.7 ksi) vs 585 MPa (84.8 ksi). In exchange, C62300 is the more ductile: elongation 25% versus 10% for C52100, and C52100 is harder (170 HB vs 160 HB). C62300 is lighter (7.65 g/cm³ vs 8.8 g/cm³ for C52100) and C62300 is stiffer (117 GPa vs 110 GPa). On the shop floor, C62300 machines more easily (fair vs poor), C62300 welds better (very good vs fair), and C62300 sits in a lower cost tier (high, $$$$) than C52100 (specialty, $$$$$).
C52100Choose it when strength drives the design.
C62300Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
C52100 vs C62300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Reduction in Area
Charpy V-Notch Impact (RT)
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Latent Heat of Fusion
Same in both: Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Castability
Same in both: Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 40%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C52100 | C62300 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C52100 vs C62300 — frequently asked
Is C52100 stronger than C62300?
Yes. C52100 has a typical yield strength of 585 MPa (84.8 ksi) against 290 MPa (42.1 ksi) for C62300 — about 102% more. Tensile strength is 660 MPa (95.7 ksi) vs 585 MPa (84.8 ksi).
Which is cheaper, C52100 or C62300?
C62300 is the lower-cost material: it sits in the high tier ($$$$) while C52100 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, C52100 or C62300?
C62300. Its machinability rates fair (45/100) against poor (30/100) for C52100; for welding the order is C62300 first (very good, 70/100) then C52100 (fair, 40/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C52100 and C62300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.