Copper Alloy C51900 vs C62580
Copper Alloy · grade comparison
Copper Alloy C51900 and C62580 are both copper alloy grades. C51900 is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 427 MPa (61.9 ksi) for C62580, about 5% more. C51900 is the more ductile: elongation 20% versus 5% for C62580, and C62580 is harder (241 HB vs 155 HB). C62580 is lighter (7.25 g/cm³ vs 8.8 g/cm³ for C51900) and C62580 runs hotter in service (300°C vs 200°C continuous). On the shop floor, C51900 welds better (fair vs poor) and C62580 sits in a lower cost tier (high, $$$$) than C51900 (specialty, $$$$$).
C51900Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
C62580Choose it when weight is the constraint, or when the part sees heat.
C51900 vs C62580: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Same in both: Machinability 25 / 100 · Machinability Rating (AISI 1212 = 100 %) 20%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 320 L/kg38.3 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C51900 | C62580 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Chrome Plating | Yes | — |
| Electropolishing | Yes | — |
| Nickel Plating | Yes | — |
| Painting | Yes | — |
| Tin Plating | Yes | — |
They share 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C51900 vs C62580 — frequently asked
Is C51900 stronger than C62580?
Yes. C51900 has a typical yield strength of 450 MPa (65.3 ksi) against 427 MPa (61.9 ksi) for C62580 — about 5% more. Tensile strength is 520 MPa (75.4 ksi) vs 772 MPa (112 ksi).
Which is cheaper, C51900 or C62580?
C62580 is the lower-cost material: it sits in the high tier ($$$$) while C51900 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, C51900 or C62580?
C51900. Its weldability rates fair (45/100) against poor (30/100) for C62580.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C51900 and C62580 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.