Copper Alloy C51100-H04 vs C51100-H08
Copper Alloy · C51100 temper comparison
C51100-H04 and C51100-H08 are two conditions of the same copper alloy grade, C51100: H04 (full hard) versus H08 (spring hard). The chemistry is identical, so every difference below comes from the condition. C51100-H08 is the stronger of the two: yield strength 530 MPa (76.9 ksi) against 435 MPa (63.1 ksi) for C51100-H04, about 22% more; tensile strength follows at 570 MPa (82.7 ksi) vs 470 MPa (68.2 ksi). In exchange, C51100-H04 is the more ductile: elongation 6% versus 3% for C51100-H08, and C51100-H08 is harder (185 HB vs 150 HB). C51100-H04 runs hotter in service (150°C vs 120°C continuous).
C51100-H04Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C51100-H08Choose it when strength drives the design.
C51100-H04 vs C51100-H08: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 110 GPa16 Msi · Shear Modulus 41 GPa5.9 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.34 · Charpy V-Notch Impact (RT) 30 J22.1 ft·lbf · Hardness, Vickers 160 HV
Physical
Density and transition temperatures.
Same in both: Density 8.86 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,060°C1,940 °F · Liquidus Temperature 1,080°C1,976 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 84 W/m·K48.5 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.8 µm/m·K9.9 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 20 % IACS · Electrical Resistivity 8.6×10⁻⁸ Ω·m3.39 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Machinability 22 / 100 · Weldability 55 / 100 · Brazeability / Solderability 90 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 60 MJ/kg25,795 BTU/lb · Embodied Carbon (primary production) 4 kg CO₂/kg · Embodied Water 320 L/kg38.3 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C51100-H04 vs C51100-H08 — frequently asked
Is C51100-H08 stronger than C51100-H04?
Yes. C51100-H08 has a typical yield strength of 530 MPa (76.9 ksi) against 435 MPa (63.1 ksi) for C51100-H04 — about 22% more. Tensile strength is 570 MPa (82.7 ksi) vs 470 MPa (68.2 ksi).
Which condition does FabDigit quote by default, H04 or H08?
H04 is the default C51100 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C51100-H04 over C51100-H08?
Pick C51100-H04 when the part is bent, formed or impact-loaded, or when the part sees heat. Pick C51100-H08 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C51100-H04 and C51100-H08 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.