Copper Alloy C50700-H01 vs C50700-H08
Copper Alloy · C50700 temper comparison
C50700-H01 and C50700-H08 are two conditions of the same copper alloy grade, C50700: H01 (quarter hard) versus H08 (spring hard). The chemistry is identical, so every difference below comes from the condition. C50700-H08 is the stronger of the two: yield strength 505 MPa (73.2 ksi) against 270 MPa (39.2 ksi) for C50700-H01, about 87% more; tensile strength follows at 550 MPa (79.8 ksi) vs 350 MPa (50.8 ksi). In exchange, C50700-H01 is the more ductile: elongation 25% versus 4% for C50700-H08, and C50700-H08 is harder (170 HB vs 103 HB). C50700-H01 runs hotter in service (200°C vs 150°C continuous). On the shop floor, C50700-H08 machines more easily (fair vs poor).
C50700-H01Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C50700-H08Choose it when strength drives the design, or when the part is machined in volume.
C50700-H01 vs C50700-H08: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 122 GPa17.7 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.89 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,025°C1,877 °F · Liquidus Temperature 1,060°C1,940 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 130 W/m·K75.1 BTU/hr·ft·°F · Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.8 µm/m·K9.9 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V · Corrosion Resistance 65 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 35 / 100 · Brazeability / Solderability 90 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C50700-H01 vs C50700-H08 — frequently asked
Is C50700-H08 stronger than C50700-H01?
Yes. C50700-H08 has a typical yield strength of 505 MPa (73.2 ksi) against 270 MPa (39.2 ksi) for C50700-H01 — about 87% more. Tensile strength is 550 MPa (79.8 ksi) vs 350 MPa (50.8 ksi).
Which condition does FabDigit quote by default, H01 or H08?
H08 is the default C50700 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C50700-H01 or C50700-H08?
C50700-H08. Its machinability rates fair (35/100) against poor (25/100) for C50700-H01.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C50700-H01 and C50700-H08 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.