Copper Alloy C47940-H02 vs C47940-M30
Copper Alloy · C47940 temper comparison
C47940-H02 and C47940-M30 are two conditions of the same copper alloy grade, C47940: H02 (half hard) versus M30 (as hot extruded). The chemistry is identical, so every difference below comes from the condition. C47940-H02 is the stronger of the two: yield strength 345 MPa (50 ksi) against 180 MPa (26.1 ksi) for C47940-M30, about 92% more; tensile strength follows at 495 MPa (71.8 ksi) vs 415 MPa (60.2 ksi). In exchange, C47940-M30 is the more ductile: elongation 38% versus 20% for C47940-H02, and C47940-H02 is harder (145 HB vs 105 HB). C47940-M30 runs hotter in service (200°C vs 180°C continuous).
C47940-H02Choose it when strength drives the design.
C47940-M30Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C47940-H02 vs C47940-M30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Shear Modulus 38 GPa5.5 Msi · Bulk Modulus 112 GPa16.2 Msi · Poisson's Ratio 0.34 · Charpy V-Notch Impact (RT) 45 J33.2 ft·lbf · Hardness, Vickers 112 HV
Physical
Density and transition temperatures.
Same in both: Density 8.41 g/cm³0.3 lb/in³ · Melting Point (Solidus) 885°C1,625 °F · Liquidus Temperature 900°C1,652 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 116 W/m·K67 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.9 µm/m·K11.6 µin/in·°F · Latent Heat of Fusion 175 J/g75.2 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 26 % IACS · Electrical Resistivity 6.6×10⁻⁸ Ω·m2.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V · Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 25 / 100 · Castability 45 / 100 · Brazeability / Solderability 80 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 260 L/kg31.2 gal/lb · Typical Recycled Content 50%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C47940-H02 vs C47940-M30 — frequently asked
Is C47940-H02 stronger than C47940-M30?
Yes. C47940-H02 has a typical yield strength of 345 MPa (50 ksi) against 180 MPa (26.1 ksi) for C47940-M30 — about 92% more. Tensile strength is 495 MPa (71.8 ksi) vs 415 MPa (60.2 ksi).
Which condition does FabDigit quote by default, H02 or M30?
M30 is the default C47940 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C47940-H02 or C47940-M30?
C47940-H02, by a small margin. Both rate good for machinability — 62/100 against 55/100 for C47940-M30.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C47940-H02 and C47940-M30 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.