Copper Alloy C42200-H02 vs C42200-H08
Copper Alloy · C42200 temper comparison
C42200-H02 and C42200-H08 are two conditions of the same copper alloy grade, C42200: H02 (half hard) versus H08 (spring hard). The chemistry is identical, so every difference below comes from the condition. C42200-H08 is the stronger of the two: yield strength 530 MPa (76.9 ksi) against 359 MPa (52.1 ksi) for C42200-H02, about 48% more; tensile strength follows at 572 MPa (83 ksi) vs 414 MPa (60 ksi). In exchange, C42200-H02 is the more ductile: elongation 12% versus 3% for C42200-H08, and C42200-H08 is harder (172 HB vs 130 HB). C42200-H02 runs hotter in service (150°C vs 120°C continuous). On the shop floor, C42200-H08 machines more easily (fair vs poor).
C42200-H02Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C42200-H08Choose it when strength drives the design, or when the part is machined in volume.
C42200-H02 vs C42200-H08: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 110 GPa16 Msi · Shear Modulus 41 GPa5.9 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.78 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,004°C1,839 °F · Liquidus Temperature 1,027°C1,881 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 113 W/m·K65.3 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.4 µm/m·K10.2 µin/in·°F · Latent Heat of Fusion 200 J/g86 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 28 % IACS · Electrical Resistivity 6.2×10⁻⁸ Ω·m2.44 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 30% · Weldability 45 / 100 · Castability 30 / 100 · Brazeability / Solderability 90 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 280 L/kg33.6 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C42200-H02 vs C42200-H08 — frequently asked
Is C42200-H08 stronger than C42200-H02?
Yes. C42200-H08 has a typical yield strength of 530 MPa (76.9 ksi) against 359 MPa (52.1 ksi) for C42200-H02 — about 48% more. Tensile strength is 572 MPa (83 ksi) vs 414 MPa (60 ksi).
Which condition does FabDigit quote by default, H02 or H08?
H02 is the default C42200 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C42200-H02 or C42200-H08?
C42200-H08. Its machinability rates fair (40/100) against poor (30/100) for C42200-H02.