Copper Alloy C38500-H01 vs C38500-H04
Copper Alloy · C38500 temper comparison
C38500-H01 and C38500-H04 are two conditions of the same copper alloy grade, C38500: H01 (quarter hard) versus H04 (full hard). The chemistry is identical, so every difference below comes from the condition. C38500-H04 is the stronger of the two: yield strength 415 MPa (60.2 ksi) against 250 MPa (36.3 ksi) for C38500-H01, about 66% more; tensile strength follows at 540 MPa (78.3 ksi) vs 440 MPa (63.8 ksi). In exchange, C38500-H01 is the more ductile: elongation 22% versus 8% for C38500-H04, and C38500-H04 is harder (150 HB vs 115 HB).
C38500-H01Choose it when the part is bent, formed or impact-loaded.
C38500-H04Choose it when strength drives the design.
C38500-H01 vs C38500-H04: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 97 GPa14.1 Msi · Shear Modulus 37 GPa5.4 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.47 g/cm³0.31 lb/in³ · Melting Point (Solidus) 875°C1,607 °F · Liquidus Temperature 890°C1,634 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.9 µm/m·K11.6 µin/in·°F · Latent Heat of Fusion 160 J/g68.8 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 26 % IACS · Electrical Resistivity 6.6×10⁻⁸ Ω·m2.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 60 / 100 · Brazeability / Solderability 85 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 80%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C38500-H01 vs C38500-H04 — frequently asked
Is C38500-H04 stronger than C38500-H01?
Yes. C38500-H04 has a typical yield strength of 415 MPa (60.2 ksi) against 250 MPa (36.3 ksi) for C38500-H01 — about 66% more. Tensile strength is 540 MPa (78.3 ksi) vs 440 MPa (63.8 ksi).
Which condition does FabDigit quote by default, H01 or H04?
As Extruded is the default C38500 condition in the FabDigit quote flow (neither H01 nor H04). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C38500-H01 over C38500-H04?
Pick C38500-H01 when the part is bent, formed or impact-loaded. Pick C38500-H04 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C38500-H01 and C38500-H04 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.