Copper Alloy C36000-H02 vs C36000-M30
Copper Alloy · C36000 temper comparison
C36000-H02 and C36000-M30 are two conditions of the same copper alloy grade, C36000: H02 (half hard) versus M30 (as hot extruded). The chemistry is identical, so every difference below comes from the condition. C36000-H02 is the stronger of the two: yield strength 310 MPa (45 ksi) against 125 MPa (18.1 ksi) for C36000-M30, about 148% more; tensile strength follows at 385 MPa (55.8 ksi) vs 340 MPa (49.3 ksi). In exchange, C36000-M30 is the more ductile: elongation 45% versus 22% for C36000-H02, and C36000-H02 is harder (115 HB vs 85 HB).
C36000-H02Choose it when strength drives the design.
C36000-M30Choose it when the part is bent, formed or impact-loaded.
C36000-H02 vs C36000-M30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 97 GPa14.1 Msi · Shear Modulus 37 GPa5.4 Msi · Bulk Modulus 105 GPa15.2 Msi · Poisson's Ratio 0.31
Physical
Density and transition temperatures.
Same in both: Density 8.5 g/cm³0.31 lb/in³ · Melting Point (Solidus) 885°C1,625 °F · Liquidus Temperature 900°C1,652 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 115 W/m·K66.4 BTU/hr·ft·°F · Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.5 µm/m·K11.4 µin/in·°F · Latent Heat of Fusion 160 J/g68.8 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 20 / 100 · Castability 55 / 100 · Brazeability / Solderability 85 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 220 L/kg26.4 gal/lb · Typical Recycled Content 80%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C36000-H02 vs C36000-M30 — frequently asked
Is C36000-H02 stronger than C36000-M30?
Yes. C36000-H02 has a typical yield strength of 310 MPa (45 ksi) against 125 MPa (18.1 ksi) for C36000-M30 — about 148% more. Tensile strength is 385 MPa (55.8 ksi) vs 340 MPa (49.3 ksi).
Which condition does FabDigit quote by default, H02 or M30?
H02 is the default C36000 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C36000-H02 or C36000-M30?
C36000-H02, by a small margin. Both rate excellent for machinability — 100/100 against 95/100 for C36000-M30.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C36000-H02 and C36000-M30 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.