Copper Alloy C35600-H02 vs C35600-O60
Copper Alloy · C35600 temper comparison
C35600-H02 and C35600-O60 are two conditions of the same copper alloy grade, C35600: H02 (half hard) versus O60 (soft annealed). The chemistry is identical, so every difference below comes from the condition. C35600-H02 is the stronger of the two: yield strength 340 MPa (49.3 ksi) against 115 MPa (16.7 ksi) for C35600-O60, about 196% more; tensile strength follows at 425 MPa (61.6 ksi) vs 340 MPa (49.3 ksi). In exchange, C35600-O60 is the more ductile: elongation 50% versus 15% for C35600-H02, and C35600-H02 is harder (130 HV vs 80 HV). C35600-O60 runs hotter in service (200°C vs 180°C continuous). On the shop floor, C35600-H02 machines more easily (100 vs 90 out of 100).
C35600-H02Choose it when strength drives the design, or when the part is machined in volume.
C35600-O60Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C35600-H02 vs C35600-O60: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 97 GPa14.1 Msi · Shear Modulus 37 GPa5.4 Msi · Bulk Modulus 112 GPa16.2 Msi · Poisson's Ratio 0.34 · Hardness, Brinell 125 HB
Physical
Density and transition temperatures.
Same in both: Density 8.47 g/cm³0.31 lb/in³ · Melting Point (Solidus) 885°C1,625 °F · Liquidus Temperature 899°C1,650 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 115 W/m·K66.4 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.5 µm/m·K11.4 µin/in·°F · Latent Heat of Fusion 160 J/g68.8 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 26 % IACS · Electrical Resistivity 6.6×10⁻⁸ Ω·m2.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.26 V · Corrosion Resistance 45 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 100% · Weldability 20 / 100 · Castability 60 / 100 · Brazeability / Solderability 85 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 320 L/kg38.3 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C35600-H02 vs C35600-O60 — frequently asked
Is C35600-H02 stronger than C35600-O60?
Yes. C35600-H02 has a typical yield strength of 340 MPa (49.3 ksi) against 115 MPa (16.7 ksi) for C35600-O60 — about 196% more. Tensile strength is 425 MPa (61.6 ksi) vs 340 MPa (49.3 ksi).
Which condition does FabDigit quote by default, H02 or O60?
H02 is the default C35600 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C35600-H02 or C35600-O60?
C35600-H02, by a small margin. Both rate excellent for machinability — 100/100 against 90/100 for C35600-O60.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C35600-H02 and C35600-O60 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.